Development of the Ni-based Metallic glassy bipolar plates for Proton Exchange Membrane Fuel Cell (PEMFC)

Alloy optimization in the Ni80-xCrxP16B4 (x = 9–30 at%) alloy system was conducted in order to achieve low Tg, Tx and a large ΔTx. From this study, the Ni65Cr15P16B4 glassy alloy was found to be the optimal alloy. The static and potentiodynamic corrosion behaviours of this alloy were measured. As a result of polarization measurements, it was found that the current density of the non-polished glassy alloy sample was smaller than that of a SUS316L sample. By contrast, the current density of the surface-polished glassy sample was slightly larger than that of the SUS316L sample in the voltage range of 0.3–0.8 V. A bipolar plate was successfully produced by hot-pressing the glassy alloy sheet in a supercooled liquid state. The I-V characteristics of a single cell with the glassy bipolar plates were measured.