Investigation of mechanical shock testing of lead-free SAC solder joints in fine pitch BGA package

Abstract The lead-free Sn–Ag–Cu (SAC 305/405) solder that replaced the tin–lead eutectic solder tends to be more brittle in nature due to high stiffness and excessive solder interfacial reactions. This leads to higher occurrences of solder joints failure during surface mount assembly and handling operations as a result of PCB bending, shock impact and drop. In this work, mechanical tests simulating the shock impact were conducted on lead-free SAC of different weight percentages. These SAC materials were prepared for use in the solder joints of fine pitch ball grid array (BGA) components which were mounted onto the motherboard. After the mechanical shock tests, strain measurements were performed on the BGA components to gauge the solder joint integrity, which was shown to be related with the formation of intermetallics in the bulk and at the interface of the SAC solder. The ball pull tests were conducted to determine both the bulk and interfacial strength and the solder joint fracture, which was classified as either mode 1, 2 or 3. A correlation was made between the silver (Ag) and copper (Cu) weight percentages with the metallurgical reactions.

[1]  L. Qiao,et al.  Measurement of fracture toughness of nickel phosphorus coatings , 2006 .

[2]  H. Saka,et al.  TEM observation of interfaces in a solder joint in a semiconductor device , 2002 .

[3]  E. Bradley,et al.  A novel mechanical shock test method to evaluate lead-free BGA solder joint reliability , 2005, Proceedings Electronic Components and Technology, 2005. ECTC '05..

[4]  Zhong Chen,et al.  Solid state interfacial reaction of Sn–37Pb and Sn–3.5Ag solders with Ni–P under bump metallization , 2004 .

[5]  J. Kivilahti,et al.  Effect of dissolution and intermetallic formation on the reliability of FC joints , 1998 .

[6]  D. R. Frear,et al.  Solder reaction-assisted crystallization of electroless Ni-P under bump metallization in low cost flip chip technology , 1999 .

[7]  K. Tu,et al.  Six cases of reliability study of Pb-free solder joints in electronic packaging technology , 2002 .

[8]  Vesa Vuorinen,et al.  Interfacial reactions between lead-free SnAgCu solder and Ni(P) surface finish on printed circuit boards , 2002 .

[9]  Anurag Bansal,et al.  FLEXURAL STRENGTH OF BGA SOLDER JOINTS WITH ENIG SUBSTRATE FINISH USING 4-POINT BEND TEST , 2005 .

[10]  Fubin Song,et al.  Brittle Failure Mechanism of SnAgCu and SnPb Solder Balls during High Speed Ball Shear and Cold Ball Pull Tests , 2007, 2007 Proceedings 57th Electronic Components and Technology Conference.

[11]  Tomi Laurila,et al.  Interfacial reactions between lead-free solders and common base materials , 2005 .

[12]  D. Goyal,et al.  Failure mechanism of brittle solder joint fracture in the presence of electroless nickel immersion gold (ENIG) interface , 2002, 52nd Electronic Components and Technology Conference 2002. (Cat. No.02CH37345).

[13]  Peter Borgesen,et al.  The growth of intermetallic compounds at Sn-Ag-Cu solder/Cu and Sn-Ag-Cu solder/Ni interfaces and the associated evolution of the solder microstructure , 2001 .

[14]  Young-Doo Jeon,et al.  Studies on Ni-Sn intermetallic compound and P-rich Ni layer at the electroless nickel UBM-solder interface and their effects on flip chip solder joint reliability , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[15]  S. Wang,et al.  Retarding growth of Ni3P crystalline layer in Ni(P) substrate by reacting with Cu-bearing Sn(Cu) solders , 2003 .

[16]  J. Kivilahti,et al.  Use of multicomponent phase diagrams for predicting phase evolution in solder/conductor systems , 2001 .