Low-loss, high-voltage 6H-SiC epitaxial p-i-n diode

The p-i-n diodes were fabricated using 31 /spl mu/m thick n/sup -/- and p-type 6H-SiC epilayers grown by horizontal cold-wall chemical vapor deposition (CVD) with nitrogen and aluminum doping, respectively. The diode exhibited a very high breakdown voltage of 4.2 kV with a low on-resistance of 4.6 m/spl Omega/cm/sup 2/. This on-resistance is lower (by a factor of five) than that of a Si p-i-n diode with a similar breakdown voltage. The leakage current density was substantially lower even at high temperatures. The fabricated SiC p-i-n diode showed fast switching with a turn-off time of 0.18 /spl mu/s at 300 K. The carrier lifetime was estimated to be 0.64 /spl mu/s at 300 K, and more than 5.20 /spl mu/s at 500 K. Various characteristics of SiC p-i-n diodes which have an advantage of lower power dissipation owing to conductivity modulation were investigated.

[1]  D. Stephani,et al.  1700 V SiC Schottky Diodes Scaled to 25 A , 2001 .

[2]  Pavel Ivanov,et al.  High voltage SiC diodes with small recovery time , 2000 .

[3]  Yoshitaka Sugawara,et al.  6.2KV 4H-SiC pin Diode with Low Forward Voltage Drop , 2000 .

[4]  Anne Henry,et al.  SiC power devices for high voltage applications , 1999 .

[5]  Tsunenobu Kimoto,et al.  Performance limiting surface defects in SiC epitaxial p-n junction diodes , 1999 .

[6]  P. Friedrichs,et al.  Switching behaviour of fast high voltage SiC pn-diodes , 1998, Proceedings of the 10th International Symposium on Power Semiconductor Devices and ICs. ISPSD'98 (IEEE Cat. No.98CH36212).

[7]  Philip G. Neudeck,et al.  Perimeter governed minority carrier lifetimes in 4H-SiC p+n diodes measured by reverse recovery switching transient analysis , 1998 .

[8]  Tsunenobu Kimoto,et al.  Step-controlled epitaxial growth of SiC: High quality homoepitaxy , 1997 .

[9]  Anne Henry,et al.  A 4.5 kV 6H silicon carbide rectifier , 1995 .

[10]  Philip G. Neudeck,et al.  2000 V 6H-SIC P-N JUNCTION DIODES GROWN BY CHEMICAL VAPOR DEPOSITION , 1994 .

[11]  B. J. Baliga,et al.  Comparison of 6H-SiC, 3C-SiC, and Si for power devices , 1993 .

[12]  Shyh Wang,et al.  Fundamentals of semiconductor theory and device physics , 1989 .

[13]  J. Palmour,et al.  Conductivity Anisotropy in Epitaxial 6H and 4H Sic , 1994 .

[14]  D. A. Fraser,et al.  The physics of semiconductor devices , 1986 .

[15]  and as an in , 2022 .