High-frequency ferromagnetic inductors covered by as-deposited FeCoAlO films with stress-induced uniaxial anisotropy

Abstract Nanocrystalline FeCoAlO films with composition gradients of Al and O were prepared by gradient sputtering (GS) method at room temperature. A uniaxial magnetic anisotropy (UMA) with high anisotropy field Hk up to 20.5 kA/m were achieved by controlling the composition gradient of doping elements Al and O. Experimental and calculated results revealed that the UMA can be attributed to the uniaxial stress gradient, which is resulted from the composition gradient. It is interesting to note that as-deposited GS films without magnetic annealing exhibited promising high-frequency ferromagnetic properties with resonance frequency over 3 GHz. The GS ferromagnetic films were used to fabricate magnetic inductors at room temperature. Significant enhancements of inductance L and Q factor were obtained in magnetic inductors covered by FeCoAlO GS films. Increments of L and Q are about 14% and 62%, respectively, at 2.4 GHz. The cut-off frequency of magnetic inductors was up to 4.6 GHz.

[1]  Magnetostriction and magnetic anisotropy of FeCo/Au multilayers , 2000 .

[2]  K. Yamasawa,et al.  Application Of Nanocrystalline Fe- Or (CoFe)-Hf-O Magnetic Films With High Electrical Resistivity To A Micro DC-DC Converter , 1997, 1997 IEEE International Magnetics Conference (INTERMAG'97).

[3]  M. Yamaguchi,et al.  Ultrahigh-frequency ferromagnetic properties of FeCoHf films deposited by gradient sputtering , 2008 .

[4]  K. Seemann,et al.  Soft ferromagnetic thin films for high frequency applications , 2002 .

[5]  Chong-Oh Kim,et al.  High frequency permeability of soft magnetic CoFeAlO films with high resistivity , 2005 .

[6]  M. Fujimoto,et al.  Multilayer nanogranular magnetic thin films for GHz applications , 2002 .

[7]  N. Sun,et al.  Stress, microstructure, and magnetic softness of high saturation magnetization (Bs) FeCoN films , 2005 .

[8]  G. Herzer,et al.  Grain size dependence of coercivity and permeability in nanocrystalline ferromagnets , 1990, International Conference on Magnetics.

[9]  M. Fujimoto,et al.  Thin film inductor for GHz band with CoFeSiO/SiO/sub 2/ multi-layer granular films and its application for power amplifier module , 2003, Digest of INTERMAG 2003. International Magnetics Conference (Cat. No.03CH37401).

[10]  Shan X. Wang,et al.  High-frequency microinductors with amorphous magnetic ground planes , 2002 .

[11]  Masahiro Yamaguchi,et al.  MICROFABRICATION AND CHARACTERISTICS OF MAGNETIC THIN-FILM INDUCTORS IN THE ULTRAHIGH FREQUENCY REGION , 1999 .

[12]  M. Yamaguchi,et al.  Effects of boron contents on magnetic properties of Fe-Co-B thin films , 2004, IEEE transactions on magnetics.

[13]  K. Arai,et al.  Sandwich type ferromagnetic RF integrated inductor , 2001, 2001 IEEE MTT-S International Microwave Sympsoium Digest (Cat. No.01CH37157).

[14]  J. Duh,et al.  High-frequency ferromagnetic properties of as-deposited FeCoZr films with uniaxial magnetic anisotropy , 2008 .

[15]  O. Ishii,et al.  High frequency magnetic properties of CoFe/SiO/sub 2/ multilayer film with the inverse magnetostrictive effect , 1994 .

[16]  D. Byun,et al.  Nanogranular Co-Fe-Al-O sputtered thin films for magnetoelastic device applications in the GHz frequency range , 2004 .

[17]  Sungho Jin,et al.  High frequency properties of Fe–Cr–Ta–N soft magnetic films , 1997 .