Uniform titanium dioxide (TiO 2) microcapsules prepared by glass membrane emulsification with subsequent solvent evaporation

Anatase-type titanium dioxide (TiO 2) was encapsulated using an Shirasu porous glass (SPG) membrane emulsification technique and followed by solvent evaporation. The oil phase, consisting of fine powder of anatase TiO 2, Disperbyk-180, the hydrophobic oil phase additive, and polymer wall solution, was pushed through the membrane pores into the aqueous phase of poly(vinyl alcohol) and sodium dodecyl sulfate to form the solid-in-oil-in water, (S/O)/W, emulsion droplets. Three types of styrene-based copolymer poly(styrene- co -acrylic acid) (PS-AA), poly(styrene- co -2-ethyl hexyl acrylate) (PS-2EHA) and poly(styrene- co -dimethyl aminoethylmethacrylate) (PS-DMAEMA) were used as an encapsulating shell. Uniform droplets were successfully obtained by modifying the oil phase using methyl laurate or hexadecanol as the oil phase additive, together with carefully monitoring the emulsification flow rate during the emulsification. The (S/O)/W emulsion was gently stirred in a sealed reactor, and evacuation of solvent started under moderate heating with increasing a vacuum intensity. Those uniform-sized TiO 2 microcapsules revealed fine porous morphologies on their surfaces as a result of a mild phase separation induced from the addition of the oil phase additive. The encapsulation efficiency was influenced by the stability of TiO 2 in the oil phase, the polymer wall employed, and the operational control of the glass membrane emulsification process. The membrane emulsification process could prepare the TiO 2 microcapsules with about ~6-8.5 wt% of encapsulation loadings. PS-AA and PS-2EHA copolymers provided better encapsulation efficiency compared to PS-DMAEMA. SPG membranes with 1.42, 2.8, 5.25, 7.0, or 9.5 #181;m were employed and 2-20 #181;m microcapsules were subsequently obtained.

[1]  W. Higuchi,et al.  Physical degradation of emulsions via the molecular diffusion route and the possible prevention thereof. , 1962, Journal of pharmaceutical sciences.

[2]  A. Herk,et al.  Polymerization of MMA at the surface of inorganic submicron particles , 1989 .

[3]  R. Schmid,et al.  Preparation and biochemical and biomedical applications of new monosized polymer particles , 1993 .

[4]  M. Iso,et al.  Synthesis and applications of porous spg (shirasu porous glass) microspheres , 1995 .

[5]  M. Nagai,et al.  Membrane emulsification a versatile tool for the synthesis of polymeric microspheres , 2000 .

[6]  M. Nagai,et al.  Microencapsulation of Fine Titanium Dioxide Powders from (S/O)/W Emulsion with Subsequent Solvent Evaporation , 2001 .

[7]  E. Sudoł,et al.  Encapsulation of inorganic particles via miniemulsion polymerization. II. Preparation and characterization of styrene miniemulsion droplets containing TiO2 particles , 2000 .

[8]  M. Nagai,et al.  Magnetite (Fe3O4) microcapsules prepared using a glass membrane and solvent removal. , 2001, Journal of microencapsulation.

[9]  Xiaohong Li,et al.  Synthesis of magnetic polymer microspheres and application for immobilization of proteinase of balillus sublitis , 1995 .

[10]  S. Omi Preparation of monodisperse microspheres using the Shirasu porous glass emulsification technique , 1996 .

[11]  David F. Ollis,et al.  Photocatalytic degradation of organic water contaminants: Mechanisms involving hydroxyl radical attack , 1990 .

[12]  P. F. Onyon Polymer Handbook , 1972, Nature.

[13]  A. Herk Encapsulation of Inorganic Particles , 1997 .

[14]  M. Nagai,et al.  Mechanism of suspension polymerization of uniform monomer droplets prepared by glass membrane (Shirasu Porous Glass) emulsification technique , 2000 .

[15]  M. Nagai,et al.  Preparation and analysis of uniform emulsion droplets using SPG membrane emulsification technique , 2000 .

[16]  E. Sudoł,et al.  Encapsulation of inorganic particles via miniemulsion polymerization. III. Characterization of encapsulation , 2000 .

[17]  D. Ollis,et al.  Heterogeneous photocatalysis: Degradation of dilute solutions of dichloromethane (CH2Cl2), chloroform (CHCl3), and carbon tetrachloride (CCl4) with illuminated TiO2 photocatalyst , 1983 .

[18]  David F. Ollis,et al.  Photoassisted heterogeneous catalysis: the degradation of trichloroethylene in water , 1983 .

[19]  D. V. Krevelen,et al.  Properties of polymers : correlations with chemical structure , 1972 .