Improved field emission properties of thiolated multi-wall carbon nanotubes on a flexible carbon cloth substrate.

In this paper we report the observation of enhanced field emission properties from thiolated multi-wall carbon nanotubes (MWCNTs) produced by a simple and effective two-step chemical surface modification technique. This technique implements carboxylation and thiolation on the MWCNTs synthesized by microwave plasma chemical vapor deposition (MPCVD) on the flexible carbon cloth substrate. The resulting thiolated MWCNTs were found to have a very low threshold field value of 1.25 V µm(-1) and a rather high field enhancement factor of 1.93 × 10(4), which are crucial for applications in versatile vacuum microelectronics.

[1]  Gehan A. J. Amaratunga,et al.  Fabrication and electrical characteristics of carbon nanotube field emission microcathodes with an integrated gate electrode , 2002 .

[2]  Young Hee Lee,et al.  Fully sealed, high-brightness carbon-nanotube field-emission display , 1999 .

[3]  Mi Chen,et al.  Microwave digestion and acidic treatment procedures for the purification of multi-walled carbon nanotubes , 2005 .

[4]  Yong‐Tae Kim,et al.  Surface thiolation of carbon nanotubes as supports: A promising route for the high dispersion of Pt nanoparticles for electrocatalysts , 2006 .

[5]  Dapeng Yu,et al.  Morphological effects on the field emission of ZnO nanorod arrays , 2005 .

[6]  Y. Saito,et al.  Field emission from carbon nanotubes and its application to electron sources , 2000 .

[7]  S. Iijima.  Helical microtubules of graphitic carbon , 1991, Nature.

[8]  H. Dai,et al.  Self-oriented regular arrays of carbon nanotubes and their field emission properties , 1999, Science.

[9]  Manton J. Guers,et al.  Ultraviolet-curable polymers with chemically bonded carbon nanotubes for microelectromechanical system applications , 2002 .

[10]  Sungho Jin,et al.  In situ-grown carbon nanotube array with excellent field emission characteristics , 2000 .

[11]  Shui-Tong Lee,et al.  Very low-field emission from aligned and opened carbon nanotube arrays , 2001 .

[12]  Xingzhong Zhao,et al.  Field emission from carbon nanotube bundle arrays grown on self-aligned ZnO nanorods , 2007 .

[13]  D. Resasco,et al.  Single-walled carbon nanotubes of controlled diameter and bundle size and their field emission properties. , 2005, The journal of physical chemistry. B.

[14]  C. Zhi,et al.  Synthesis and field-electron-emission behavior of aligned GaAs nanowires , 2005 .

[15]  X. W. Sun,et al.  Stable field emission from hydrothermally grown ZnO nanotubes , 2006 .

[16]  Gehan A. J. Amaratunga,et al.  Self-Aligned, Gated Arrays of Individual Nanotube and Nanowire Emitters , 2004 .

[17]  Wenzhi Li,et al.  Field emission of carbon nanotubes grown on carbon cloth , 2004 .

[18]  Z. Ren,et al.  Enhanced Field Emission of ZnO Nanowires , 2004 .

[19]  Omkaram Nalamasu,et al.  Contact transfer of aligned carbon nanotube arrays onto conducting substrates , 2006 .

[20]  Sundara Ramaprabhu,et al.  Performance of polymer electrolyte membrane fuel cells with carbon nanotubes as oxygen reduction catalyst support material , 2005 .

[21]  Dezhi Wang,et al.  Field emission of silicon nanowires , 2006 .

[22]  Thomas Stöckli,et al.  Field emission from carbon nanotubes: the first five years , 2001 .

[23]  C. Chen,et al.  Growth and characteristics of carbon nanotubes on carbon cloth as electrodes , 2005 .

[24]  W. D. de Heer,et al.  A Carbon Nanotube Field-Emission Electron Source , 1995, Science.

[25]  Pavel Nikolaev,et al.  From Fullerenes to Nanotubes , 1996 .

[26]  P. Papakonstantinou,et al.  Surface‐to‐Depth Analysis of Functionalized Multi‐Wall Carbon Nanotubes (FMWCNTS) , 2005 .