Finite element modeling of plasticity-induced crack closure with emphasis on geometry and mesh refinement effects

Abstract Two-dimensional, elastic–perfectly plastic finite element analyses of middle-crack tension (MT) and compact tension (CT) geometries were conducted to study fatigue crack closure and to calculate the crack-opening values under plane-strain and plane-stress conditions. The behaviors of the CT and MT geometries were compared. The loading was selected to give the same maximum stress intensity factor in both geometries, and thus approximately similar initial forward plastic zone sizes. Mesh refinement studies were performed on both geometries with various element types. For the CT geometry, negligible crack-opening loads under plane-strain conditions were observed. In contrast, for the MT specimen, the plane-strain crack-opening stresses were found to be significantly larger. This difference was shown to be a consequence of in-plane constraint. Under plane-stress conditions, it was found that the in-plane constraint has negligible effect, such that the opening values are approximately the same for both the CT and MT specimens.

[1]  J. Rice,et al.  Limitations to the small scale yielding approximation for crack tip plasticity , 1974 .

[2]  E. Wolf.  Fatigue crack closure under cyclic tension , 1970 .

[3]  Kiyotsugu Ohji,et al.  INFLUENCE OF MECHANICAL FACTORS ON THE FATIGUE CRACK CLOSURE , 1977 .

[4]  Robert McClung,et al.  On the finite element analysis of fatigue crack closure—1. Basic modeling issues , 1989 .

[5]  R. C. McClung,et al.  On the finite element analysis of fatigue crack closure—2. Numerical results , 1989 .

[6]  B. H. Thacker,et al.  Finite element visualization of fatigue crack closure in plane stress and plane strain , 1991, International Journal of Fracture.

[7]  B. Dattaguru,et al.  EXPERIMENTAL AND ANALYTICAL ESTIMATES OF FATIGUE CRACK CLOSURE IN AN ALUMINIUM‐COPPER ALLOY PART II: A FINITE ELEMENT ANALYSIS , 1997 .

[8]  S. R. Daniewicz,et al.  Determination of the opening load for a growing fatigue crack: evaluation of experimental data reduction techniques and analytical models , 2002 .

[9]  Donald R. Houser,et al.  An elastic-plastic analytical model for predicting fatigue crack growth in arbitrary edge-cracked two-dimensional geometries with residual stress , 1994 .

[10]  R. Mcclung,et al.  Fatigue Crack Closure and Crack Growth Outside the Small Scale Yielding Regime , 1988 .

[11]  Anders Blom,et al.  An experimental and numerical study of crack closure , 1985 .

[12]  R. C. McClung,et al.  FINITE ELEMENT ANALYSIS OF SPECIMEN GEOMETRY EFFECTS ON FATIGUE CRACK CLOSURE , 1994 .

[13]  A. J. Carlsson,et al.  Influence of non-singular stress terms and specimen geometry on small-scale yielding at crack tips in elastic-plastic materials , 1973 .

[14]  J. C. Rice,et al.  On numerically accurate finite element solutions in the fully plastic range , 1990 .

[15]  John R. Rice,et al.  Mechanics of Crack Tip Deformation and Extension by Fatigue , 1967 .

[16]  J. Newman.  A Finite-Element Analysis of Fatigue Crack Closure , 1976 .

[17]  J. Padovan,et al.  Fatigue crack propagation and closure behavior of modified 1070 steel: Finite element study , 1997 .

[18]  Norman A. Fleck,et al.  Finite element analysis of plasticity-induced crack closure under plane strain conditions , 1986 .

[19]  Ken Gall,et al.  Plastic zones and fatigue-crack closure under plane-strain double slip , 1996 .

[20]  Andrew H. Sherry,et al.  COMPENDIUM OF T‐STRESS SOLUTIONS FOR TWO AND THREE DIMENSIONAL CRACKED GEOMETRIES , 1995 .

[21]  A. Kfouri,et al.  An elastic-plastic finite element analysis of a compact tension specimen , 1983 .

[22]  R. Mcclung.  The influence of applied stress, crack length, and stress intensity factor on crack closure , 1991 .

[23]  Ji-Ho Song,et al.  DETERMINATION OF THE MOST APPROPRIATE MESH SIZE FOR A 2‐D FINITE ELEMENT ANALYSIS OF FATIGUE CRACK CLOSURE BEHAVIOUR , 1997 .

[24]  N. Fleck,et al.  Analysis of Crack Closure Under Plane Strain Conditions , 1988 .