Experimental and numerical study of size effect on long-term drying behavior of concrete: influence of drying depth

This study aims at rationalizing the analysis of drying shrinkage tests and taking better advantage of the measurements, by studying the influence of the specimen size. Three self-consolidating concrete and one vibrated concrete mixes were studied during 3 years. Drying started 24 h after casting. The tests were carried on three sizes of cylinders: Φ78, Φ113 and Φ163 mm, under the same experimental conditions (20 ± 1 °C, 50 ± 5 % relative humidity), according to RILEM recommendations. The results show that the classification of concrete depends not only on the experimental conditions, but also on the duration of the shrinkage measurement. A scientific approach based on a simple mathematical model was proposed to analyze shrinkage data. The ultimate drying shrinkage did not depend on specimen size. The existing empirical models of shrinkage and drying used in construction codes take into account the size effect only through a geometrical parameter called notional size of cross-section, assuming that concrete is an homogeneous and non-aging material. With the time variable change by the ratio of the square root of the time and the notional size of cross-section, a master curve can be found for the theoretical curves of different sizes. However, experimentally, upshifts were observed between the drying shrinkage curves for different specimens sizes, thus phenomena that occur at early age are not taken into account by current models. The drying depth notion was introduced to explain the part of drying behavior responsible for the observed difference between drying curves. The influence of this concrete layer on the long-term behavior was confirmed by a two-step modeling of the mass-loss evolution. The first one included coupled drying-hydration model. The same classification was observed numerically and experimentally, with higher drying kinetics corresponding to smaller specimens, but the experimental shift could not be reproduced. The drying depth notion was incorporated in the second model; an increase in permeability was introduced in the outer layer of the concrete specimens. The size effect on the long-term mass-loss was reproduced numerically.

[1]  John A. Bickley,et al.  Design for durability: The key to improving concrete sustainability , 2014 .

[2]  Farid Benboudjema,et al.  Interaction between drying, shrinkage, creep and cracking phenomena in concrete , 2005 .

[3]  D. Bentz.  Three-Dimensional Computer Simulation of Portland Cement Hydration and Microstructure Development , 1997 .

[4]  Z. P. Bažant,et al.  Nonlinear water diffusion in nonsaturated concrete , 1972 .

[5]  Senot Sangadji,et al.  PREDICTION MODEL FOR SHRINKAGE OF LIGHTWEIGHT AGGREGATE CONCRETE , 2009 .

[6]  B. Mobasher,et al.  Experimental observations of early-age drying of Portland cement paste under low-pressure conditions , 2011 .

[7]  Kristek,et al.  Measurement of time-dependent strains of concrete. Prepared by subcommittee 4: Standardized test methods for creep and shrinkage , 1998 .

[8]  A. Loukili,et al.  Hydration kinetics, change of relative humidity, and autogenous shrinkage of ultra-high-strength concrete , 1999 .

[9]  L. Taerwe,et al.  FIB model code for concrete structures 2010 , 2013 .

[10]  Will Hansen,et al.  Effect of Specimen Size and Shape on Drying Shrinkage of Concrete , 1987 .

[11]  E. Rozière,et al.  Influence of Formwork Duration on the Shrinkage, Microstructure, and Durability of Cement-Based Materials , 2015 .

[12]  J. Quirk,et al.  Permeability of porous solids , 1961 .

[13]  Olivier Coussy,et al.  ROLE OF AIR PRESSURE IN DRYING OF WEAKLY PERMEABLE MATERIALS , 2001 .

[14]  M. Thiéry,et al.  A Model for Hydration‐Drying Interactions in the Concrete Cover , 2013 .

[15]  Zdeněk P. Baǎnt,et al.  Effect of cracking in drying and shrinkage specimens , 1982 .

[16]  S. Bonnet,et al.  Effect of uniaxial compressive loading on gas permeability and chloride diffusion coefficient of concrete and their relationship , 2013 .

[17]  Ahmed Loukili,et al.  Effect of the water saturation of aggregates on the shrinkage induced cracking risk of concrete at early age , 2014 .

[18]  Alain Sellier,et al.  Multiphasic Finite Element Modeling of Concrete Hydration , 2007 .

[19]  S. A. Al-Saleh,et al.  Effects of drying conditions, admixtures and specimen size on shrinkage strains , 2006 .

[20]  Bernhard A. Schrefler,et al.  Hygro‐thermo‐chemo‐mechanical modelling of concrete at early ages and beyond. Part I: hydration and hygro‐thermal phenomena , 2006 .

[21]  David A Lange,et al.  Relative Humidity in Concrete , 2006 .

[22]  Zdenek P. Bazant,et al.  Statistical Extrapolation of Shrinkage Data - Part II : Bayesian Updating , 1987 .

[23]  Vincent Picandet,et al.  Crack Effects on Gas and Water Permeability of Concretes , 2009 .

[24]  O. Coussy.  Poromechanics: Coussy/Poromechanics , 2005 .

[25]  T. Adam.  Influence of the relative humidity on the hydration kinetics of concrete , 2006 .

[26]  Alain Sellier,et al.  Toward a better comprehension and modeling of hysteresis cycles in the water sorption-desorption process for cement based materials , 2011 .

[27]  M. Pigeon,et al.  Influence of key parameters on drying shrinkage of cementitious materials , 1999 .

[28]  Ahmed Loukili,et al.  Influence of shrinkage-reducing admixtures on plastic and long-term shrinkage , 2011 .

[29]  Denis Mitchell,et al.  Material performance lessons , 2008 .

[30]  P. C. Kreijger.  The skin of concrete composition and properties , 1984 .

[31]  Will Hansen,et al.  ULTIMATE DRYING SHRINKAGE OF CONCRETE-INFLUENCE OF MAJOR PARAMETERS , 1987 .

[32]  H. Samouh.  Nouvelles approches des relations entre formulation et comportement différé des matériaux cimentaires : application aux bétons autoplaçants , 2015 .

[33]  J. I. Escalante-García,et al.  Nonevaporable water from neat OPC and replacement materials in composite cements hydrated at different temperatures , 2003 .

[34]  M. D. Nguyen.  Modélisation des couplages entre hydratation et dessiccation des matériaux cimentaires à l'issue du décoffrage. Étude de la dégradation des propriétés de transfert , 2009 .

[35]  K. Pruess,et al.  TOUGH2 User's Guide Version 2 , 1999 .

[36]  Alan H. Mattock,et al.  Influence of Size and Shape of Member on the Shrinkage and Creep of Concrete , 1966 .

[37]  Jean-Michel Torrenti,et al.  Modeling Concrete Shrinkage under Variable Ambient Conditions , 1999 .

[38]  E. Rozière,et al.  Long-term deformations and cracking risk of concrete with high content of mineral additions , 2012 .

[39]  S. Granger,et al.  Influence of paste volume on shrinkage cracking and fracture properties of self-compacting concrete , 2007 .

[40]  Véronique Baroghel-Bouny,et al.  Modélisation du séchage des bétons , 2007 .

[41]  Z. Bažant,et al.  Creep and shrinkage prediction model for analysis and design of concrete structures-model B3 , 1995 .

[42]  Roman Wendner,et al.  The B4 Model for Multi-decade Creep and Shrinkage Prediction , 2013 .

[43]  I. Carol,et al.  Modeling of drying shrinkage of concrete specimens at the meso-level , 2011 .

[44]  Richard E. Weyers,et al.  Development of a shrinkage performance specifications and prediction model analysis for supplemental cementitious material concrete mixtures , 2005 .

[45]  Roman Wendner,et al.  Progress in Creep and Shrinkage Prediction Engendered by Alarming Bridge Observations and Expansion of Laboratory Database , 2013 .

[46]  Luc Taerwe,et al.  fib model code for concrete structures 2010 , 2013 .

[47]  Z. Bažant,et al.  STATISTICAL EXTRAPOLATION OF SHRINKAGE DATA - PART I: REGRESSION , 1987 .

[48]  W. Hansen,et al.  Prediction of concrete drying shrinkage from short-term measurements , 1989 .

[49]  Farid Benboudjema,et al.  Analysis of microcracking induced by differential drying shrinkage , 2008 .

[50]  D. Bentz,et al.  Drying/hydration in cement pastes during curing , 2001 .

[51]  In-Seok Yoon,et al.  Prediction of Temperature Distribution in High-Strength Concrete Using Hydration Model , 2008 .

[52]  Cruz Alonso,et al.  Mathematical Modeling of a Concrete Surface Skin Effect on Diffusion in Chloride Contaminated Media , 1997 .