Preparation and properties of palmitic-stearic acid eutectic mixture/expanded graphite composite as phase change material for energy storage

A novel composite PCM (phase change material) with PA-SA (palmitic-stearic acid) eutectic mixture as PCM and EG (expanded graphite) as supporting material was prepared. The optimum absorption ratio of PA-SA/EG (Palmitic-stearic acid/expanded graphite) composite PCM was determined as PA-SA:EG = 13:1 (by mass). Scanning electron microscope and Fourier transformation infrared spectroscopy results show that PA-SA was uniformly distributed in the porous network structure of EG due to the physical action. Thermal property and thermal stability of the PA-SA/EG composite PCM were characterized by DSC (differential scanning calorimetry) and TGA (thermogravimetric analysis). DSC results indicated that the melting and freezing temperatures and latent heats of PA-SA/EG were measured as 53.89 °C and 54.37 °C, and 166.27 J/g and 166.13 J/g. TGA test results revealed that PA-SA/EG had a good thermal stability in working temperature range. Thermal cycling test results showed PA-SA/EG had a good thermal reliability after 720 thermal cycles. Thermal conductivity of the composite PCM was measured as 2.51 W/m K, much higher than that of PA-SA. The thermal energy storage and release rates of PA-SA/EG were also increased due to the high thermal conductivity of EG. In conclusion, the prepared PA-SA/EG composite PCM can be acted as a potential material for thermal energy storage due to the acceptable thermal properties, good thermal reliability and stability, high thermal conductivity.

[1]  Zhaolin Gu,et al.  Thermal energy recovery of air conditioning system¿¿heat recovery system calculation and phase change materials development , 2004 .

[2]  Y. Varol,et al.  Energy and exergy analysis of a latent heat storage system with phase change material for a solar collector , 2008 .

[3]  W. Tao,et al.  Fatty acids as phase change materials: A review , 2014 .

[4]  Bing Zhang,et al.  Preparation of capric acid/halloysite nanotube composite as form-stable phase change material for thermal energy storage , 2011 .

[5]  Ruzhu Wang,et al.  Enhancement of heat transfer for thermal energy storage application using stearic acid nanocomposite with multi-walled carbon nanotubes , 2013 .

[6]  Changzhong Chen,et al.  Morphology and thermal properties of electrospun fatty acids/polyethylene terephthalate composite fibers as novel form-stable phase change materials , 2008 .

[7]  Yu Yanping,et al.  Theoretic Prediction of Melting Temperature and Latent Heat for a Fatty Acid Eutectic Mixture , 2011 .

[8]  Hongfa Di,et al.  Application of latent heat thermal energy storage in buildings: State-of-the-art and outlook , 2007 .

[9]  A. Sari,et al.  Preparation, thermal properties and thermal reliability of eutectic mixtures of fatty acids/expanded vermiculite as novel form-stable composites for energy storage , 2010 .

[10]  G. Ziskind,et al.  Numerical investigation of a PCM-based heat sink with internal fins , 2005 .

[11]  A. Sari,et al.  Lauric and palmitic acids eutectic mixture as latent heat storage material for low temperature heating applications , 2005 .

[12]  M. Hussein,et al.  Nano-encapsulated organic phase change material based on copolymer nanocomposites for thermal energy storage , 2014 .

[13]  Huaqing Xie,et al.  Increasing the thermal conductivity of palmitic acid by the addition of carbon nanotubes , 2010 .

[14]  A. Celzard,et al.  Surface area of compressed expanded graphite , 2002 .

[15]  Wei Li,et al.  Fabrication and morphological characterization of microencapsulated phase change materials (MicroPCMs) and macrocapsules containing MicroPCMs for thermal energy storage , 2012 .

[16]  Dong Zhang,et al.  Experimental study on the phase change behavior of phase change material confined in pores , 2007 .

[17]  V. V. Tyagi,et al.  PCM thermal storage in buildings: A state of art , 2007 .

[18]  A. Sari,et al.  Thermal conductivity improvement of stearic acid using expanded graphite and carbon fiber for energy storage applications , 2007 .

[19]  A. Sari,et al.  Phase change and heat transfer characteristics of a eutectic mixture of palmitic and stearic acids as PCM in a latent heat storage system , 2003 .

[20]  Hui Li,et al.  Preparation and characterization of stearic acid/expanded graphite composites as thermal energy storage materials , 2010 .

[21]  Liwu Fan,et al.  Thermal conductivity enhancement of phase change materials for thermal energy storage: A review , 2011 .

[22]  Jianguo Zhao,et al.  Microstructure and thermal properties of a paraffin/expanded graphite phase-change composite for thermal storage , 2011 .

[23]  Lei Cao,et al.  Synthesis and thermal properties of shape-stabilized lauric acid/activated carbon composites as phase change materials for thermal energy storage , 2012 .

[24]  Yi Wang,et al.  Effect of preparation methods on the structure and thermal properties of stearic acid/activated montmorillonite phase change materials , 2012 .

[25]  A. Sari,et al.  Thermal conductivity and latent heat thermal energy storage characteristics of paraffin/expanded graphite composite as phase change material , 2007 .

[26]  Yong Zhao,et al.  Electrospun ultrafine composite fibers consisting of lauric acid and polyamide 6 as form-stable phase change materials for storage and retrieval of solar thermal energy , 2012 .

[27]  Yanping Yuan,et al.  Preparation and properties of myristic–palmitic–stearic acid/expanded graphite composites as phase change materials for energy storage , 2014 .