Mechanical property degradation of high crystalline SiC fiber–reinforced SiC matrix composite neutron irradiated to ∼100 displacements per atom

Abstract For the development of silicon carbide (SiC) materials for next-generation nuclear structural applications, degradation of material properties under intense neutron irradiation is a critical feasibility issue. This study evaluated the mechanical properties and microstructure of a chemical vapor infiltrated SiC matrix composite, reinforced with a multi-layer SiC/pyrolytic carbon–coated Hi-NicalonTM Type S SiC fiber, following neutron irradiation at 319 and 629 °C to ∼100 displacements per atom. Both the proportional limit stress and ultimate flexural strength were significantly degraded as a result of irradiation at both temperatures. After irradiation at 319 °C, the quasi-ductile fracture behavior of the nonirradiated composite became brittle, a result that was explained by a loss of functionality of the fiber/matrix interface associated with the disappearance of the interphase due to irradiation. The specimens irradiated at 629 °C showed increased apparent failure strain because the fiber/matrix interphase was weakened by irradiation-induced partial debonding.

[1]  W. Johnson,et al.  Influence of chemical driving forces in ion mixing of metallic bilayers , 1984 .

[2]  S. Pennycook,et al.  Direct determination of the chemical bonding of individual impurities in graphene. , 2012, Physical review letters.

[3]  R. Naslain,et al.  The design of the fibre-matrix interfacial zone in ceramic matrix composites , 1998 .

[4]  Kerr Fitzgerald,et al.  Review of SiCf/SiCm corrosion, erosion and erosion-corrosion in high temperature helium relevant to GFR conditions , 2018 .

[5]  Y. Katoh,et al.  Concentric ring on ring test for unirradiated and irradiated miniature SiC specimens , 2011 .

[6]  C. Back,et al.  Characterization of SiC–SiC composites for accident tolerant fuel cladding , 2015 .

[7]  K. Ozawa,et al.  Irradiation-induced shrinkage of highly crystalline SiC fibers , 2015 .

[8]  Steven J. Zinkle,et al.  Materials Challenges in Nuclear Energy , 2013 .

[9]  A. Evans,et al.  Matrix fracture in fiber-reinforced ceramics , 1986 .

[10]  Toyohiko Yano,et al.  X-ray diffractometry and high-resolution electron microscopy of neutron-irradiated SiC to a fluence of 1.9×1027 n/m2 , 1998 .

[11]  William A. Curtin,et al.  THEORY OF MECHANICAL-PROPERTIES OF CERAMIC-MATRIX COMPOSITES , 1991 .

[12]  Lance Lewis Snead,et al.  High dose neutron irradiation of Hi-Nicalon Type S silicon carbide composites, Part 1: Microstructural evaluations , 2015 .

[13]  Nathan M George,et al.  Neutronic analysis of candidate accident-tolerant cladding concepts in pressurized water reactors , 2015 .

[14]  N. Bansal.  Handbook of Ceramic Composites , 2005 .

[15]  U. Fischer,et al.  Conceptual design of the dual-coolant blanket in the frame of the EU power plant conceptual study , 2003 .

[16]  Frank W. Zok,et al.  The physics and mechanics of fibre-reinforced brittle matrix composites , 1994, Journal of Materials Science.

[17]  H. Miura,et al.  Improved tokamak concept focusing on easy maintenance , 1998 .

[18]  William J. Weber,et al.  Displacement damage in silicon carbide irradiated in fission reactors , 2004 .

[19]  Lance Lewis Snead,et al.  Evaluation of neutron irradiated silicon carbide and silicon carbide composites , 2007 .

[20]  Y. Katoh,et al.  Microstructural defects in SiC neutron irradiated at very high temperatures , 2008 .

[21]  W. J. Weber,et al.  Atomistic Study of Intrinsic Defect Migration in 3C-SiC , 2004 .

[22]  J. Lamon,et al.  Analysis of crack deviation in ceramic matrix composites and multilayers based on the Cook and Gordon mechanism , 2007 .

[23]  C. Sauder.  Ceramic Matrix Composites: Nuclear Applications , 2014 .

[24]  C. Sauder,et al.  Chemical compatibility between UO 2 fuel and SiC cladding for LWRs. Application to ATF (Accident-Tolerant Fuels) , 2017 .

[25]  Y. Katoh,et al.  Stability of SiC and its composites at high neutron fluence , 2011 .

[26]  J. Kaae.  The Mechanical Behavior of Biso-Coated Fuel Particles during Irradiation. Part I: Analysis of Stresses and Strains Generated in the Coating of a Biso Fuel Particle during Irradiation , 1977 .

[27]  S. Jitsukawa,et al.  Effect of displacement damage up to 50 dpa on microstructural development in SiC/SiC composites , 2007 .

[28]  Lance Lewis Snead,et al.  High-dose neutron irradiation of Hi-Nicalon Type S silicon carbide composites. Part 2: Mechanical and physical properties , 2015 .

[29]  R. Averback,et al.  Radiation-enhanced diffusion in Ni/Zr diffusion couples , 1988 .

[30]  S. Du,et al.  The critical issues of SiC materials for future nuclear systems , 2018 .

[31]  T. Suzuki,et al.  Microstructure and annealing behavior of heavily neutron-irradiated β-SiC , 1988 .

[32]  T. Yano,et al.  Physical property change of heavily neutron-irradiated Si3N4 and SiC by thermal annealing , 2001 .

[33]  Daejong Kim,et al.  Fabrication and measurement of hoop strength of SiC triplex tube for nuclear fuel cladding applications , 2015 .

[34]  S. Zinkle,et al.  Measurement of the effect of radiation damage to ceramic composite interfacial strength , 1992 .

[35]  K. Terrani,et al.  Silicon carbide composite for light water reactor fuel assembly applications , 2014 .

[36]  H. Trinkaus,et al.  Helium accumulation in metals during irradiation – where do we stand? , 2003 .

[37]  A. Kohyama,et al.  Microstructural evolution analysis of NITE SiC/SiC composite using TEM examination and dual-ion irradiation , 2007 .

[38]  Steven J. Zinkle,et al.  An overview of dual coolant Pb–17Li breeder first wall and blanket concept development for the US ITER-TBM design , 2006 .

[39]  W. Hillig,et al.  The effect of fiber-matrix debond energy on the matrix cracking strength and the debond shear strength , 1990 .