Growth of high quality AlN on sapphire by using a low-temperature AlN interlayer

Aluminum nitride is a material of great potential for high power electronic devices, UV photonic devices as well as acoustic devices. However, the lack of a good crystal growth technology for bulk material and substrate hinders the development of these AlN-based devices. While AlN has been successfully grown on sapphire substrate for some time, the presence of a large number of dislocations in the material is still a major barrier to overcome [1]. In this work, we demonstrate a low-dislocation-density AlN template on sapphire by inserting an AlN interlayer by metal-organic chemical vapor deposition. The main idea of our approach is to change the growth mode in the course of the epitaxial growth by decreasing growth temperature and changing V/III ratio. As the growth mode changes, dislocations tend to be redirected and/or form dipole half loops via annihilation processes [2]. The etch-pit-density of the AlN templates is reduced from 3.6×109 cm-2 to 1.7×109 cm-2. Accordingly, the full width at half maximum of the (0002) x-ray rocking curve is reduced from 37 arcsec to 12 arcsec. The result indicates that the AlN template has low screw and mixed type dislocations. AlGaN/GaN Schottky diodes fabricated on this high quality AlN template exhibit very high breakdown voltage (> 2000 V), which sets a record-high figure of merit of 1.15 GW/cm2.

[1]  E. C. Carr,et al.  CORRELATION OF CATHODOLUMINESCENCE INHOMOGENEITY WITH MICROSTRUCTURAL DEFECTS IN EPITAXIAL GAN GROWN BY METALORGANIC CHEMICAL-VAPOR DEPOSITION , 1997 .

[2]  M. Asif Khan,et al.  Improved performance of 325-nm emission AlGaN ultraviolet light-emitting diodes , 2003 .

[3]  M. Asif Khan,et al.  Low pressure metalorganic chemical vapor deposition of AIN over sapphire substrates , 1992 .

[4]  M. Khan,et al.  Reduction of threading dislocation densities in AlN∕sapphire epilayers driven by growth mode modification , 2006 .

[5]  O. Ambacher,et al.  Wet chemical etching of AlN in KOH solution , 2006 .

[6]  James S. Speck,et al.  Role of threading dislocation structure on the x‐ray diffraction peak widths in epitaxial GaN films , 1996 .

[7]  W. Schaff,et al.  Low density of threading dislocations in AlN grown on sapphire , 2007 .

[8]  S. Kamiyama,et al.  Microstructure of epitaxial lateral overgrown AlN on trench-patterned AlN template by high-temperature metal-organic vapor phase epitaxy , 2006 .

[9]  David W. Weyburne,et al.  Correlation between optoelectronic and structural properties and epilayer thickness of AlN , 2007 .

[10]  Motoaki Iwaya,et al.  Growth of high-quality and crack free AlN layers on sapphire substrate by multi-growth mode modification , 2007 .

[11]  Y. Xi,et al.  Very high quality AlN grown on (0001) sapphire by metal-organic vapor phase epitaxy , 2006 .

[12]  S. Kamiyama,et al.  High-Temperature Metal-Organic Vapor Phase Epitaxial Growth of AlN on Sapphire by Multi Transition Growth Mode Method Varying V/III Ratio , 2006 .

[13]  Masataka Imura,et al.  Dislocations in AlN Epilayers Grown on Sapphire Substrate by High-Temperature Metal-Organic Vapor Phase Epitaxy , 2007 .

[14]  A. G. Cullis,et al.  A study of dislocations in AlN and GaN films grown on sapphire substrates , 2005 .

[15]  Richard J. Molnar,et al.  Inhomogeneous spatial distribution of reverse bias leakage in GaN Schottky diodes , 2001 .

[16]  S. Kamiyama,et al.  Annihilation mechanism of threading dislocations in AlN grown by growth form modification method using V/III ratio , 2007 .