Strength and fracture of Si micropillars: A new scanning electron microscopy-based micro-compression test

A novel method for in situ scanning electron microscope (SEM) micro-compression tests is presented. The direct SEM observation during the instrumented compression testing allows for very efficient positioning and assessment of the failure mechanism. Compression tests on micromachined Si pillars with volumes down to 2 μm3 are performed inside the SEM, and the results demonstrate the potential of the method. In situ observation shows that small diameter pillars tend to buckle while larger ones tend to crack before failure. Compressive strength increases with decreasing pillar diameter and reaches almost 9 GPa for submicrometer diameter pillars. This result is in agreement with earlier bending experiments on Si. Difficulties associated with precise strain measurements are discussed.

[1]  E. J. Hearn,et al.  Mechanics of materials: An introduction to the mechanics of elastic and plastic deformation of solids and structural components , 1977 .

[2]  Patrick Schwaller,et al.  Observation of fracture and plastic deformation during indentation and scratching inside the scanning electron microscope , 2004 .

[3]  K. T. Ramesh,et al.  The Design of Accurate Micro-Compression Experiments , 2006 .

[4]  O. Tabata,et al.  Specimen size effect on tensile strength of surface-micromachined polycrystalline silicon thin films , 1998 .

[5]  G. A. Hegemier,et al.  Strain softening of rock, soil and concrete — a review article , 1984 .

[6]  E. Arzt.  Size effects in materials due to microstructural and dimensional constraints: a comparative review , 1998 .

[7]  Stefan Johansson,et al.  In situ tensile strength measurement and Weibull analysis of thick film and thin film micromachined polysilicon structures , 1997 .

[8]  Y. Isono,et al.  Evaluation of size effect on mechanical properties of single crystal silicon by nanoscale bending test using AFM , 2000, Journal of Microelectromechanical Systems.

[9]  Huma Ashraf,et al.  Advanced silicon etching using high-density plasmas , 1995, Photonics West - Micro and Nano Fabricated Electromechanical and Optical Components.

[10]  Joseph F Labuz,et al.  Continuum fracture mechanics of uniaxial compression on brittle materials , 1998 .

[11]  Ioannis Vardoulakis,et al.  GEOMETRIC SOFTENING IN TRIAXIAL TESTS ON GRANULAR MATERIAL , 1982 .

[12]  R. L. Edwards,et al.  Measurements of Young's modulus, Poisson's ratio, and tensile strength of polysilicon , 1997, Proceedings IEEE The Tenth Annual International Workshop on Micro Electro Mechanical Systems. An Investigation of Micro Structures, Sensors, Actuators, Machines and Robots.

[13]  T. Kenny,et al.  Fracture toughness and crack growth phenomena of plasma-etched single crystal silicon , 2000 .

[14]  D. Dimiduk,et al.  Sample Dimensions Influence Strength and Crystal Plasticity , 2004, Science.

[15]  W. Weibull.  A statistical theory of the strength of materials , 1939 .

[16]  O. Zienkiewicz,et al.  Rock mechanics in engineering practice , 1968 .

[17]  N. N. Nemeth,et al.  Probabilistic Weibull behavior and mechanical properties of MEMS brittle materials , 2003 .

[18]  L. Pook.  Mechanical behavior of materials: Engineering methods for deformation, fracture, and fatigue , 1997 .

[19]  R. Mullen,et al.  The fracture toughness of polysilicon microdevices: A first report , 1997 .

[20]  J. Schweitz,et al.  Micromechanical fracture strength of silicon , 1990 .

[21]  T. Tanaka,et al.  Nano-scale bending test of Si beam for MEMS , 2000, Proceedings IEEE Thirteenth Annual International Conference on Micro Electro Mechanical Systems (Cat. No.00CH36308).

[22]  Oliver Kraft,et al.  Mechanical Testing of Thin Films and Small Structures , 2001 .