High heat flux tests on heat sinks armored with tungsten rods

Abstract This paper presents the results of high heat flux tests at Sandia National Laboratories of mock-ups armored with W rods embedded in water-cooled copper-alloy heat sinks. The major result is the excellent performance of these mock-ups in thermal response tests at up to 30 MW/m2 and in thermal cycling tests of 500 cycles (10 s on, 10 s off) at ∼25 MW/m2. Melting of rod tips and the subsequent ‘self-repair’ of a degraded thermal bond were seen. Issues for further development in both testing and manufacturing of the mock-ups were identified. Evaluation of the surface heat flux was found to be somewhat problematic and this issue is discussed.

[1]  Kazuyuki Nakamura,et al.  Examination of material performance of W exposed to high heat load: Postmortem analysis of W exposed to TEXTOR plasma and E-beam test stand , 1997 .

[2]  K. F. Mast,et al.  Tungsten as target material in fusion devices , 1996 .

[3]  Eliseo Visca,et al.  Overview of the EU small scale mock-up tests for ITER high heat flux components , 1998 .

[4]  R. Neu,et al.  The tungsten experiment in ASDEX Upgrade , 1997 .

[5]  V. A. Belyakov,et al.  Development of plasma facing components for ITER at Efremov Institute , 1997, 17th IEEE/NPSS Symposium Fusion Engineering (Cat. No.97CH36131).

[6]  S. Suzuki,et al.  Development of divertor high heat flux components at JAERI , 1997, 17th IEEE/NPSS Symposium Fusion Engineering (Cat. No.97CH36131).

[7]  J. M. McDonald,et al.  High heat flux testing capabilities at Sandia National Laboratories - New Mexico , 1994 .

[8]  J. M. McDonald,et al.  Recent results of high heat flux testing at the Plasma Materials Test Facility , 1996, Optics & Photonics.

[9]  G. Vieider,et al.  Development of tungsten armor and bonding to copper for plasma-interactive components , 1998 .

[10]  V. Philipps,et al.  Impurity release from high Z test limiters immersed in TEXTOR-94 edge plasmas , 1997 .

[11]  R. Neu,et al.  A review of recent experiments on W and high Z materials as plasma-facing components in magnetic fusion devices , 1996 .

[12]  K.T. Slattery,et al.  Development of tungsten brush structures for PFC armor applications , 1997, 17th IEEE/NPSS Symposium Fusion Engineering (Cat. No.97CH36131).

[13]  Kazuyuki Nakamura,et al.  Thermal fatigue tests on CVD-W/Cu divertor mock-ups , 1998 .