We have observed growth‐ and processing‐related defects and optically induced degradation in In1−xGaxAsyP1−y double‐heterostructure material intended for 1.2–1.3‐μm laser diodes. Threshold for the degradation observed decreases with increasing layer thickness, suggesting a relation to strain arising from compositional variation during growth.

[1] B. W. Hakki,et al. Degradation of CW GaAs double-heterojunction lasers at 300 K , 1973 .

[2] P. Petroff,et al. Nature of optically induced defects in Ga1−xAlxAs–GaAs double‐heterojunction laser structures , 1974 .

[3] A. Ballman,et al. Liquid phase epitaxial In1−xGaxAsyP1−y lattice matched to 〈100〉 InP over the complete wavelength range 0.92⩽λ⩽1.65 μm , 1978 .

[4] R. Dixon,et al. Laser‐excited photoluminescence of three‐layer GaAs double‐heterostructure laser material , 1975 .

[5] W. D. Johnston. Macroscopic deterioration of fluorescence from AlxGa1−xAs–GaAs DH material following microscopic physical damage , 1974 .

[6] R. Ito,et al. A Simple Method for Obtaining Luminescent Pattern of Double Heterostructure Crystals , 1973 .

[7] B. Miller,et al. Degradation characteristics of cw optically pumped AlxGa1−xAs heterostructure lasers , 1973 .