Verification of an airframe fatigue life monitoring system using ex-service structure

Abstract In this paper the verification of the Royal Australian Air Force's (RAAF) F/A-18 Hornet Airframe Service Life Monitoring system is summarised. The availability of a significant number of RAAF ex-service centre fuselage sections with known usage facilitated this effort. Using an enhanced teardown procedure, in-service crack growth was identified at a significant number of locations. By comparing measured in-service growth with full scale fatigue test-demonstrated growth, and fitting failure distributions to the in-service data, the effectiveness of the monitoring system in maintaining a specific probability of failure was assessed.

[1]  Edward E. Cureton,et al.  Unbiased Estimation of the Standard Deviation , 1968 .

[2]  Simon Barter,et al.  Interpreting fatigue test results using a probabilistic fracture approach , 2005 .

[3]  L. Molent,et al.  The Canadian and Australian F/A-18 International Follow-On Structural Test Project , 2002 .

[5]  Russell Wanhill,et al.  The lead crack fatigue lifing framework , 2011 .

[6]  B. Aktepe,et al.  Review of fatigue monitoring of agile military aircraft , 2000 .

[7]  Lorrie Molent.  Alternative methods for derivation of safe life limits for a 7050-T7451 aluminium alloy structure , 2015 .

[8]  L. Molent,et al.  The equivalence of EPS and EIFS based on the same crack growth life data , 2015 .

[9]  R Core Team,et al.  R: A language and environment for statistical computing. , 2014 .

[10]  Lorrie Molent,et al.  Verification of an individual aircraft fatigue monitoring system , 2012 .

[11]  Lorrie Molent,et al.  An experimental evaluation of fatigue crack growth , 2005 .

[12]  Russell Wanhill,et al.  Typical fatigue-initiating discontinuities in metallic aircraft structures , 2012 .

[13]  K. J. Miller,et al.  What is fatigue damage? A view point from the observation of low cycle fatigue process , 2005 .

[14]  L. Molent,et al.  Ex-Service F/A-18 Centre Barrel Fatigue Flaw Identification Test Plan , 2003 .

[15]  Lorrie Molent,et al.  A study of fatigue variability in aluminium alloy 7050-T7451 , 2016 .

[16]  L. Molent,et al.  A review of equivalent pre-crack sizes in aluminium alloy 7050-T7451 , 2014 .

[17]  Lorrie Molent,et al.  A comparison of crack growth behaviour in several full-scale airframe fatigue tests , 2007 .