HIGH STRAIN RATE SHEAR EVALUATION AND CHARACTERIZATION OF AISI D2 TOOL STEEL IN ITS HARDENED STATE

High strain rate mechanical testing on fully hardened AISI D2 tool steel (at 62 HRc) was performed utilizing the Compressive Split Hopkinson Bar technique (CSHB) incorporating a punching shear strain state. The high strain rate conditions were comparable to those encountered in machining processes, with shear strain rates on the order of 5 × 104 s−1 and shear strains in excess of unity (100% mm/mm). The tests were performed at various initial temperatures ranging from 296–873 K to investigate the flow stress behavior of the hardened tool steel as a function of temperature. The high strain rate experimental shear stress-strain data was used to fit the flow stress by; i) an empirically based constitutive law in the form proposed by Johnson and Cook; as well as, (ii) a physically based constitutive law proposed by Zerilli and Armstrong which accounts for strain, strain rate, and temperature dependence of flow stress. The data incorporated the adiabatic temperature rise in the shear zone and was used in the constitutive law modeling. The deformed microstructure was investigated using optical and scanning electron microscopy to determine the extent of the shear localization zone and the final fracture mode.

[1]  Michael J. Worswick,et al.  Adiabatic Shear in annealed and shock-hardened iron and in quenched and tempered 4340 steel , 2001 .

[2]  Hossam A. Kishawy,et al.  Surface Integrity of Die Material in High Speed Hard Machining, Part 2: Microhardness Variations and Residual Stresses , 2000 .

[3]  Hossam A. Kishawy,et al.  Surface Integrity of Die Material in High Speed Hard Machining, Part 1: Micrographical Analysis , 2000 .

[4]  P. Clayton,et al.  High-speed five-axis milling of hardened tool steel , 2000 .

[5]  Spfc Serge Jaspers Metal cutting mechanics and material behaviour , 1999 .

[6]  Tom Childs,et al.  MATERIAL PROPERTY NEEDS IN MODELING METAL MACHINING , 1998 .

[7]  Yung C. Shin,et al.  Material Constitutive Modeling Under High Strain Rates and Temperatures Through Orthogonal Machining Tests , 1997, Manufacturing Science and Engineering: Volume 2.

[8]  M. Worswick,et al.  Adiabatic Shear in Remco Iron and Quenched and Tempered 4340 Steel , 1997 .

[9]  M. Elbestawi,et al.  A Model for Chip Formation During Machining of Hardened Steel , 1996 .

[10]  Marc A. Meyers,et al.  DYNAMIC RECRYSTALLIZATION IN HIGH-STRAIN, HIGH-STRAIN-RATE PLASTIC DEFORMATION OF COPPER , 1994 .

[11]  Yi-long Bai,et al.  Adiabatic Shear Localization: Occurrence, Theories and Applications , 1992 .

[12]  R. Armstrong,et al.  Dislocation-mechanics-based constitutive relations for material dynamics calculations , 1987 .

[13]  J. Nutting,et al.  Deformation of metals to high strains using combination of torsion and compression , 1984 .

[14]  G. R. Johnson,et al.  Response of Various Metals to Large Torsional Strains Over a Large Range of Strain Rates—Part 1: Ductile Metals , 1983 .

[15]  M. Staker,et al.  The relation between adiabatic shear instability strain and material properties , 1981 .

[16]  A. Cottrell,et al.  Strong solids , 1964, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.