论文信息 - Synthesis of elastomeric nanoparticles via microemulsion polymerization

Synthesis of elastomeric nanoparticles via microemulsion polymerization

Copolymerization of butyl acrylate (BuA) with dimethyl‐meta‐isopropenylbenzyl isocyanate (TMI) was carried out at 40°C in microemulsions stabilized with a mixture of sodium dodecyl sulfate and sodium bis(2‐ethylhexyl) sulfosuccinate (3/1 w/w). The mixture of monomers was dosed during polymerization. An inverse dependence of particle diameter (DP) on the dosing rate of monomers and the TMI concentration was found. Polymer content close to 25 wt% and a DP between 40 and 50 nm were obtained. J. VINYL ADDIT. TECHNOL., 11:132–134, 2005. © 2005 Society of Plastics Engineers

M. E. Treviño‐Martínez | L. F. Ramos‐de Valle | R. G. López-Campos | Y. del Angel‐Vargas

[1] K. Tauer,et al. Studies on semibatch microemulsion polymerization of butyl acrylate: Influence of the potassium peroxodisulfate concentration , 2004 .

[2] T. Guo,et al. Toughening modification of PS with n-BA/MMA/styrene core-shell structured copolymer from emulsifier-free emulsion polymerization , 2003 .

[3] C. Bucknall. Blends containing core-shell impact modifiers Part 1. Structure and tensile deformation mechanisms (IUPAC Technical Report) , 2001 .

[4] B. Brooks,et al. Semibatch emulsion polymerization of butyl acrylate. I. Effect of monomer distribution , 1999 .

[5] M. El-Aasser,et al. Emulsion terpolymerization of dimethyl meta‐isopropenyl benzyl isocyanate (TMI®) with acrylic monomers: Process development and kinetics , 1996 .

[6] M. Schneider,et al. Structured latex particles as impact modifiers for poly(styrene–co-acrylonitrile) blends , 1996 .