Tribological behavior of dual-layer electroless-plated Ag–carbon nanotube coatings

Abstract The tribological behavior of electroless Ag-plated carbon nanotube (CNT) dual-layer coatings was assessed and compared to that of the pure CNT coating. The motivation was to protect the surface of CNT coatings from wear by depositing a thin, soft Ag coating. The methods used for coating CNTs and Ag were spin coating and electroless plating, respectively. These coating methods were selected based on their simplicity and cost effectiveness. Wear tests were conducted by sliding the coatings against a stainless steel ball under a 10–30 mN applied load. Results showed that the wear rate of the dual-layer coating was strongly dependent on the thickness of the Ag layer as well as the applied load. At a 10 mN load and an Ag thickness of 65 nm, the wear rate of the dual-layer coating was about 10 times less than that of the pure CNT coating. However, when the thickness of the Ag was decreased to 11.5 nm, the wear rate was significantly higher. Also, the steady-state friction coefficients of the CNT and the dual-layer Ag–CNT coatings were in the range of 0.65–0.73 for all loads. A model of the wear reduction mechanism of the dual-layer Ag–CNT coating was proposed.

[1]  Dae-Eun Kim,et al.  Nano-scale friction: A review , 2009 .

[2]  N. Croitoru,et al.  Electroless Silver and Silver with Tungsten Thin Films for Microelectronics and Microelectromechanical System Applications , 2000 .

[3]  Yoonhwan Woo,et al.  Sensitivity analysis of plating conditions on mechanical properties of thin film for MEMS applications , 2011 .

[4]  Il-Young Kim,et al.  Friction and wear characteristics of the carbon nanotube–aluminum composites with different manufacturing conditions , 2009 .

[5]  Dae-Eun Kim,et al.  A novel approach to wear reduction of micro-components by synthesis of carbon nanotube-silver composite coating , 2011 .

[6]  V. Popov.  Carbon Nanotubes: Properties and Applications , 2006 .

[7]  Y. Kim,et al.  Effects of Self-Assembled Monolayer and PFPE Lubricant on Wear Characteristics of Flat Silicon Tips , 2008 .

[8]  N. Schell,et al.  The nanostructure evolution during and after magnetron deposition of Au films , 2003 .

[9]  Q. Xue,et al.  Investigation of tribological properties of polyimide/carbon nanotube nanocomposites , 2004 .

[10]  R. B. Rakhi,et al.  Field emission from carbon nanotubes on a graphitized carbon fabric , 2008 .

[11]  Yi Feng,et al.  Electroless plating of carbon nanotubes with silver , 2004 .

[12]  Paul K. Chu,et al.  Self-selective electroless plating: An approach for fabrication of functional 1D nanomaterials , 2008 .

[13]  A. Erdemir,et al.  Solid Lubricant Coatings: Recent Developments and Future Trends , 2004 .

[14]  L. Yoo,et al.  Conductivities of graphite fiber composites with single-walled carbon nanotube layers , 2011 .

[15]  Feng Zhou,et al.  A novel lubricant additive based on carbon nanotubes for ionic liquids , 2008 .

[16]  J. M. Martín,et al.  Super-low friction of MoS 2 coatings in various environments , 1996 .

[17]  A. Stanishevsky,et al.  Electroless silver plating on spin-coated silver nanoparticle seed layers , 2006 .

[18]  I. Sung,et al.  Surface Damage Characteristics of Self-Assembled Monolayers of Alkanethiols on Metal Surfaces , 2004 .

[19]  Dae-Eun Kim,et al.  Assessment of adhesion between thin film and silicon based on a scratch test , 2010 .

[20]  Steven T. Patton,et al.  Failure mechanisms of a MEMS actuator in very high vacuum , 2002 .