论文信息 - Liquid phase epitaxial In1−xGaxAsyP1−y lattice matched to 〈100〉 InP over the complete wavelength range 0.92⩽λ⩽1.65 μm

Liquid phase epitaxial In1−xGaxAsyP1−y lattice matched to 〈100〉 InP over the complete wavelength range 0.92⩽λ⩽1.65 μm

A two‐phase supercooled solution method is described for the LPE growth of In1−xGaxAsyP1−y on 〈100〉 InP over the entire range of lattice‐matched compositions, 0⩾y<1, 0?x<0.47. Liquid and solid compositions, distribution coefficients, and band‐gap data which may be used to design specific devices are presented.

A. Ballman | R. Nahory | M. Pollack | J. Dewinter

[1] H. Nagai,et al. InP‐GaxIn1−xAsyP1−y double heterostructure for 1.5 μm wavelength , 1978 .

[2] Y. Suematsu,et al. In 1-x Ga x As y P 1-y /InP DH lasers fabricated on InP , 1978 .

[3] K. Nakajima,et al. Phase Diagram of the In‐Ga‐As‐P Quaternary System and LPE Growth Conditions for Lattice Matching on InP Substrates , 1978 .

[4] K. Iga,et al. GaInAsP/InP DH Laser Grown by Newly Designed Vertical LPE Furnace , 1977 .

[5] S. Akiba,et al. Growth of Lattice-Matched InGaAsP/InP Double-Heterostructures by the Two-Phase Supercooled Solution Technique , 1977 .

[6] S. Akiba,et al. 500-hour CW Operation of InGaAsP/InP Double Heterostructure Lasers Fabricated on (100)-InP Substrates , 1977 .

[7] L. W. James,et al. Growth and characterization of InGaAsP–InP lattice‐matched heterojunctions , 1976 .

[8] R. Moon,et al. Growth and Characterization of InP ‐ lnGaAsP Lattice-Matched Heterojunctions , 1973 .