GaN‐based nanowires: From nanometric‐scale characterization to light emitting diodes

We studied and improved gallium nitride (GaN) nanowire (NW) based light emitting diodes (LEDs). PIN nanodiodes with and without InGaN/GaN multiple quantum wells (MQWs) were grown by molecular beam epitaxy (MBE) under N-rich conditions on n-doped Si(111) substrates. Thanks to the coalescence of the p-type region of the NWs grown at low temperature, an autoplanarization process has been performed to obtain LEDs. Ni/Au top contacts have been deposited and patterned in order to bias the devices. A multiple-scale characterization approach has been carried out through the comparison of localized cathodoluminescence (CL) and macroscopic electroluminescence (EL) spectra. It shows that the EL emission of PIN-based LED at room temperature is related to defects in the p-type region of the NWs. In order to enhance the radiative recombinations of NW-based LEDs, we have first added InGaN/GaN MQWs, and secondly an electron blocking layer (EBL) has been inserted between the MQWs and the p-type zone of the NWs. The LED with EBL exhibited an emission band at 420 nm. The blue-shift of this emission band with increasing injected current is attributed to quantum confined Stark effect (QCSE) and evidences the radiative emission of InGaN/GaN MQWs. At 50 mA dc current, this improved NW-based LED emits about 500 times more light than the heterostructure without EBL. (C) 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

[1]  Piotr Perlin,et al.  Role of the electron blocking layer in the low-temperature collapse of electroluminescence in nitride light-emitting diodes , 2007 .

[2]  Kwan Soo Chung,et al.  Nanoscale Ultraviolet‐Light‐Emitting Diodes Using Wide‐Bandgap Gallium Nitride Nanorods , 2003 .

[3]  K. Kishino,et al.  InGaN/GaN Multiple Quantum Disk Nanocolumn Light-Emitting Diodes Grown on (111) Si Substrate , 2004 .

[4]  C. Adelmann,et al.  Indium incorporation during the growth of InGaN by molecular-beam epitaxy studied by reflection high-energy electron diffraction intensity oscillations , 1999 .

[5]  K. Kishino,et al.  GaN/AlGaN nanocolumn ultraviolet light-emitting diodes grown on n-(111) Si by RF-plasma-assisted molecular beam epitaxy , 2008 .

[6]  B. Daudin,et al.  From nucleation to growth of catalyst-free GaN nanowires on thin AlN buffer layer , 2007 .

[7]  Hiroto Sekiguchi,et al.  InGaN/GaN nanocolumn LEDs emitting from blue to red , 2007, SPIE OPTO.

[8]  H. Renevier,et al.  Nucleation mechanism of GaN nanowires grown on (111) Si by molecular beam epitaxy , 2009, Nanotechnology.

[9]  M. Sánchez-García,et al.  Structural and optical characterization of intrinsic GaN nanocolumns , 2002 .

[10]  Bruce W Wessels,et al.  Behavior of 2.8- and 3.2-eV photoluminescence bands in Mg-doped GaN at different temperatures and excitation densities , 1999 .

[11]  S. Nakamura,et al.  Spontaneous emission of localized excitons in InGaN single and multiquantum well structures , 1996 .

[12]  D. Kim,et al.  High-Brightness Light Emitting Diodes Using Dislocation-Free Indium Gallium Nitride/Gallium Nitride Multiquantum-Well Nanorod Arrays , 2004 .