论文信息 - TRANSMISSION ELECTRON MICROSCOPY CHARACTERIZATION OF NANOCRYSTALLINE COPPER

TRANSMISSION ELECTRON MICROSCOPY CHARACTERIZATION OF NANOCRYSTALLINE COPPER

The microstructure and grain boundary structure of nanocrystalline Cu powders and a compact prepared by the inert-gas condensation technique have been characterized by transmission electron microscopy. The as-prepared particles are round in shape and have no distinct surface facets. Annealing twins (coherent Z3 boundaries) have been observed in the as-prepared Cu particles as well as in the compact. Pores are commonly found at grain boundaries, triple grain junctions and some in the interior of grains in the compact. In addition to twin boundaries, a number of special grain boundaries have been observed. These special grain boundaries have low-index interface planes, and sometimes have misorientation angles close to coincidence site lattice (CSL) orientations.

[1] Haydn N. G. Wadley,et al. Twin formation during the atomic deposition of copper , 1999 .

[2] M. Nastasi,et al. Observation of body centered cubic Cu in Cu/Nb nanolayered composites , 1997 .

[3] Paul G. Sanders,et al. Elastic and tensile behavior of nanocrystalline copper and palladium , 1997 .

[4] Paul G. Sanders,et al. IMPROVEMENTS IN THE SYNTHESIS AND COMPACTION OF NANOCRYSTALLINE MATERIALS , 1997 .

[5] Paul G. Sanders,et al. Structure of nanocrystalline palladium and copper studied by small angle neutron scattering , 1996 .

[6] William E. Buhro,et al. Mechanical properties of nanocrystalline copper produced by solution-phase synthesis , 1996 .

[7] Richard W. Siegel,et al. Processing and mechanical behavior of nanocrystalline Fe , 1995 .

[8] Scott A. Barnett,et al. Plastic and Elastic Properties of Compositionally Modulated Thin Films , 1994 .

[9] Ruslan Z. Valiev,et al. On the structure and strength of ultrafine-grained copper produced by severe plastic deformation , 1994 .

[10] J. Weertman,et al. Mechanical behavior of nanocrystalline Cu and Pd , 1991 .

[11] S. Lehoczky,et al. Strength enhancement in thin‐layered Al‐Cu laminates , 1978 .

[12] Paul G. Sanders,et al. Creep of nanocrystalline Cu, Pd, and Al-Zr , 1997 .

[13] M. Mayo. High and low temperature superplasticity in nanocrystalline materials , 1997 .

[14] J. Weertman,et al. Tensile strength and creep properties of nanocrystalline palladium , 1990 .