Effect of Polypropylene Fibre Addition on Properties of Geopolymers Made by 3D Printing for Digital Construction

This paper investigates the effect of polypropylene (PP) fibres on the fresh and hardened properties of 3D-printed fibre-reinforced geopolymer mortars. Different percentages of PP fibres ranging between 0.25% and 1.00% by volume were added to an optimised geopolymer mixture. All samples showed reasonable workability and extrudability. In addition, shape-retention ability in the fresh state was investigated as a major requirement for 3D-printing. The compressive strength of the printed specimens was tested in the hardened state in three loading directions, viz. longitudinal, perpendicular, and lateral. The flexural strength of samples was also tested in the longitudinal and lateral directions. In addition, the interlayer bond strength was investigated. Fibre addition seems to influence compressive strengths positively only when the loading is perpendicular to the interface plane. This is due to the preferential fibre alignment parallel to the direction of extrusion. The addition of fibre significantly enhanced the flexural performance of the printed samples. The use of fibre dosages of 0.75 and 1.00 vol % caused deflection-hardening behaviour of the 3D-printed geopolymers and, hence, a significantly higher fracture energy in comparison to specimens without fibre or with lower fibre content. However, an increase in the fibre volume caused some minor reduction in interlayer bond strength. With respect to properties in the fresh state, higher fibre volumes caused better shape-retention ability in the printed samples. The results indicate the possibility of printing fibre-reinforced geopolymers which meet all the necessary properties in both the fresh and hardened states.

[1]  Fabio Gramazio,et al.  Complex concrete structures: Merging existing casting techniques with digital fabrication , 2015, Comput. Aided Des..

[2]  Y Zhang,et al.  DEVELOPMENT OF SUSTAINABLE CEMENTITIOUS MATERIALS , 2004 .

[3]  Jay G. Sanjayan,et al.  Effect of Delay Time on the Mechanical Properties of Extrusion-Based 3D Printed Concrete , 2017 .

[4]  Ronald Rael,et al.  Developing Concrete Polymer Building Components for 3D Printing , 2011, ACADIA proceedings.

[5]  T. A. Dar,et al.  Development of Fly Ash based Geopolymer Concrete , 2017 .

[6]  Valentina Colla,et al.  Building components for an outpost on the Lunar soil by means of a novel 3D printing technology , 2014 .

[7]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[8]  Faiz Shaikh,et al.  Tensile Strain Hardening Behavior of PVA Fiber-Reinforced Engineered Geopolymer Composite , 2015 .

[9]  Ming Xia,et al.  Effect of Type of Fiber on Inter-Layer Bond and Flexural Strengths of Extrusion-Based 3D Printed Geopolymer , 2018, Materials Science Forum.

[10]  Xiangyu Wang,et al.  A critical review of the use of 3-D printing in the construction industry , 2016 .

[11]  Victor C. Li,et al.  A self-reinforced cementitious composite for building-scale 3D printing , 2018, Cement and Concrete Composites.

[12]  GramazioFabio,et al.  Complex concrete structures , 2015 .

[13]  Eric Mayer,et al.  Properties Of Concrete , 2016 .

[14]  J. Sanjayan,et al.  High ductile behavior of a polyethylene fiber-reinforced one-part geopolymer composite: A micromechanics-based investigation , 2017 .

[15]  Viktor Mechtcherine,et al.  Integration der Bewehrung beim 3D‐Druck mit Beton , 2018 .

[16]  Viktor Mechtcherine,et al.  3D-printed steel reinforcement for digital concrete construction – Manufacture, mechanical properties and bond behaviour , 2018, Construction and Building Materials.

[17]  Behrokh Khoshnevis,et al.  Automated construction by contour craftingrelated robotics and information technologies , 2004 .

[18]  Dirk Volkmer,et al.  Properties of 3D-printed fiber-reinforced Portland cement paste , 2017 .

[19]  Jay G. Sanjayan,et al.  Current progress of 3D concrete printing technologies , 2017 .

[20]  Ming Xia,et al.  Effect of surface moisture on inter-layer strength of 3D printed concrete , 2018 .

[21]  T. T. Le,et al.  Mix design and fresh properties for high-performance printing concrete , 2012 .

[22]  A. Gibb,et al.  Hardened properties of high-performance printing concrete , 2012 .

[23]  Ming Jen Tan,et al.  Additive manufacturing of geopolymer for sustainable built environment , 2017 .

[24]  D. Huntzinger,et al.  A life-cycle assessment of Portland cement manufacturing: comparing the traditional process with alternative technologies , 2009 .

[25]  Jay G. Sanjayan,et al.  Synthesis of heat and ambient cured one-part geopolymer mixes with different grades of sodium silicate , 2015 .

[26]  Viktor Mechtcherine,et al.  Developing and Testing of Strain-Hardening Cement-Based Composites (SHCC) in the Context of 3D-Printing , 2018, Materials.

[27]  Simon A. Austin,et al.  Tensile bond testing of concrete repairs , 1995 .

[28]  J. Sanjayan,et al.  Microscale investigation of fiber-matrix interface properties of strain-hardening geopolymer composite , 2017 .

[29]  Kah Fai Leong,et al.  3D printing trends in building and construction industry: a review , 2017 .

[30]  En-Hua Yang,et al.  Micromechanics-based investigation of a sustainable ambient temperature cured one-part strain hardening geopolymer composite , 2017 .

[31]  Geert De Schutter,et al.  Vision of 3D printing with concrete — Technical, economic and environmental potentials , 2018, Cement and Concrete Research.

[32]  Nicolas Roussel,et al.  Digital Concrete: Opportunities and Challenges , 2016 .