Generation of periodic surface structures on silica fibre surfaces using 405 nm CW diode lasers

Periodic surface structures have been observed on the end surfaces of synthetic silica fibres when they are exposed to long-term irradiation with light from a 405 nm CW diode laser. The surface structures are generated when the laser power is at a level which is three magnitudes of order lower than that of the damage threshold. They exhibit multiple bends, break-ups and bifurcations, unlike interference patterns but rather like the effect caused by short-pulsed laser irradiation on wide band-gap insulators. The detailed investigation undertaken in this work has concluded that the key parameters that contribute to the generation of the surface structures are power density, surface roughness, polarisation direction and the presence of ultraviolet defect centres.

[1]  Preston,et al.  Pattern formation during laser melting of silicon. , 1989, Physical review. B, Condensed matter.

[2]  E. J. Friebele,et al.  Drawing‐induced defect centers in a fused silica core fiber , 1976 .

[3]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[4]  Peter Karlitschek,et al.  Possibilities and limitations of optical fibers for the transmission of excimer laser radiation , 1997, Laser Damage.

[5]  David L. Griscom,et al.  Defect structure of glasses: Some outstanding questions in regard to vitreous silica , 1985 .

[6]  R Salimbeni,et al.  Optical fiber transmission of high power excimer laser radiation. , 1987, Applied optics.

[7]  Arai,et al.  Two types of oxygen-deficient centers in synthetic silica glass. , 1988, Physical review. B, Condensed matter.

[8]  Wei Shi,et al.  Terahertz Technology: Coherent and Widely Tunable THz and Millimeter Waves Based on Difference- Frequency Generation in GaSe and ZnGeP_2 , 2002 .

[9]  J. Reif,et al.  High power laser interaction with the surface of wide bandgap materials , 1989 .

[10]  Florenta Costache,et al.  Control parameters in pattern formation upon femtosecond laser ablation , 2007 .

[11]  Arai,et al.  Dependence of defects induced by excimer laser on intrinsic structural defects in synthetic silica glasses. , 1991, Physical review. B, Condensed matter.

[12]  Fabrizio Messina,et al.  Generation of defects in amorphous SiO2 assisted by two-step absorption on impurity sites , 2008, Journal of physics. Condensed matter : an Institute of Physics journal.

[13]  L. Skuja.  Optically active oxygen-deficiency-related centers in amorphous silicon dioxide , 1998 .

[14]  V.Kh Khalilov,et al.  Character, mechanism of formation and transformation of point defects in type IV silica glass , 1994 .

[15]  K H Jungbluth,et al.  Studies in fiber guided excimer laser surgery for cutting and drilling bone and meniscus , 1991, Lasers in surgery and medicine.

[16]  Karl-Friedrich Klein,et al.  UV fibers for applications below 200 nm , 2001, SPIE BiOS.

[17]  M. Birnbaum.  Semiconductor Surface Damage Produced by Ruby Lasers , 1965 .

[18]  Michael Bestehorn,et al.  Formation of self-organized regular nanostructures upon femtosecond laser ablation , 2004, International Symposium on Laser Precision Microfabrication.

[19]  Juergen Reif,et al.  Femtosecond laser ablation from dielectric materials: Comparison to arc discharge erosion , 1999 .

[20]  John E. Sipe,et al.  Laser-Induced Periodic Surface Structure on Solids: A Universal Phenomenon , 1982 .

[21]  Mitsunobu Miyagi,et al.  Status and improvements of UV laser scalpel , 2003, SPIE BiOS.

[22]  Fritz Keilmann,et al.  Periodic surface structures frozen into CO2 laser-melted quartz , 1982 .