Randomly selected generator bars from a 50-year-old Norwegian hydro power generator were examined in this work. Typical non-destructive tests, as partial discharge and dissipation factor measurements were initially performed at both 50 Hz and 0.1 Hz. Then, the AC breakdown strength of the epoxy/mica/glass fibre reinforced bar insulation was measured by gradually increasing the voltage in steps of 5 kV with duration of 1 min until breakdown occurred. The field graded terminations were soaked in transformer oil during breakdown testing to prevent external surface flashovers. The AC breakdown voltage ranged between 60 kV and 75 kV, which corresponds to 8-10-fold the service voltage of 7.4 kV. No significant difference in breakdown voltage was observed between bars being located close to the high voltage or neutral terminal during service. This indicates minor degradation caused by the AC service stress, even after 50 years in service. No correlations were found between the measured breakdown voltage and the diagnostic partial discharge activity and dissipation factor measurements.
[1]
Emre Kantar,et al.
Effects of Frequency and Temperature on Partial Discharge Characterization of Stator Windings
,
2020,
2020 IEEE Conference on Electrical Insulation and Dielectric Phenomena (CEIDP).
[2]
G. Berg,et al.
Partial Discharge Characterisation of Stator Windings Taken from a 50-year-old Norwegian Hydrogenerator
,
2019,
2019 IEEE Electrical Insulation Conference (EIC).
[3]
Mitsuru Onoda,et al.
Prediction of residual breakdown electrical field strength of epoxy-mica paper insulation systems for the stator winding of large generators
,
2015,
IEEE Transactions on Dielectrics and Electrical Insulation.
[4]
K. Frohlich,et al.
Insulation Failure Mechanisms of Power Generators [Feature Article]
,
2008,
IEEE Electrical Insulation Magazine.