Viscosity measurement of FeO–SiO2–V2O3–TiO2 slags in the temperature range of 1644–1791 K and modelling by using ion-oxygen parameter

ABSTRACT The viscosity of the FeO–SiO2–TiO2–V2O3 system with TiO2 between 5 and 15-mass %, V2O3 between 5 and 15-mass% and FeO/SiO2 mass ratio between 1.4 and 2.2 was measured at temperature 1644–1791 K. It was found that the viscosity of slag increased with increasing V2O3 level, decreased with increasing temperature and FeO/SiO2 ratio, and decreased with increasing TiO2 content. The viscosity values of FeO–SiO2–V2O3–TiO2 system were calculated by employing various viscosity models. The mean deviations are about 54.04, 84.13, 18.96, and 4.48% for the values by Mill, modified Riboud, and , respectively. Thus, a model based on the ion-oxygen parameter, which can describe the influence of components and temperature, provided the best fit to the viscosity data. There were three kinds of crystalline phases, Fe2SiO4, Fe2TiO4, and FeV2O4 in all samples. The SiO2 crystal appeared in Al, Al3, and B3 samples.

[1]  Lijun Wang,et al.  A Novel Process for Simultaneous Extraction of Iron, Vanadium, Manganese, Chromium, and Titanium from Vanadium Slag by Molten Salt Electrolysis , 2016 .

[2]  J. Diao,et al.  Structural Characterization of FeO–SiO2–V2O3 Slags Using Molecular Dynamics Simulations and FT-IR Spectroscopy , 2016 .

[3]  Min Chen,et al.  Viscosity Property and Structure Analysis of FeO–SiO2–V2O3–TiO2–Cr2O3 Slags , 2016 .

[4]  X. Lv,et al.  The Effect of TiO 2 on the Liquidus Zone and Apparent Viscosity of SiO 2 -CaO-8wt.%MgO-14wt.%Al 2 O 3 System , 2016 .

[5]  Lijun Wang,et al.  Estimating Electrical Conductivities of CaO-MgO-Al2O3-SiO2 Using Ion-Oxygen Parameter , 2016 .

[6]  Lijun Wang,et al.  Effects of CaO, MgO, Al2O3 and SiO2 on the carbothermic reduction of synthetic FeCr2O4 , 2015 .

[7]  S. Seetharaman,et al.  Experimental Study of Phase Equilibria in CaO–SiO2–MgO–Al2O3–V2O3 Slags , 2014 .

[8]  K. Chou,et al.  Structural Study of Glassy CaO–SiO2–CaF2–TiO2 Slags by Raman Spectroscopy and MAS-NMR , 2014 .

[9]  X. She,et al.  Viscosity and viscosity estimation model of fully liquid slags in TiO2–Al2O3–CaO–SiO2 and TiO2–Al2O3–CaO–SiO2–MgO systems with high TiO2 concentration and low mass ratio of CaO to SiO2 , 2014 .

[10]  K. Chou,et al.  Estimation of Sulfide Capacities of Multicomponent Slags using Optical Basicity , 2013 .

[11]  S. Seetharaman,et al.  Determination of Vanadium Valence State in CaO-MgO-Al2O3-SiO2 System By High-Temperature Mass Spectrometry , 2013, Metallurgical and Materials Transactions B.

[12]  Mao Chen,et al.  Viscosity Measurements of “FeO”-SiO2 Slag in Equilibrium with Metallic Fe , 2013, Metallurgical and Materials Transactions B.

[13]  Shaona Wang,et al.  A novel method to extract vanadium and chromium from vanadium slag using molten NaOH‐NaNO3 binary system , 2013 .

[14]  K. Chou,et al.  Measuring and Modeling Viscosity of CaO-Al2O3-SiO2(-K2O) Melt , 2012, Metallurgical and Materials Transactions B.

[15]  J. Diao,et al.  Nucleation and growth kinetics of spinel crystals in vanadium slag , 2012 .

[16]  X. Wang,et al.  Influence of TiO2 and basicity on viscosity of Ti bearing slag , 2012 .

[17]  I. Sohn,et al.  Effect of TiO2 on the Viscosity and Slag Structure in Blast Furnace Type Slags , 2012 .

[18]  H. Matsuura,et al.  Influence of TiO2 on the Viscous Behavior of Calcium Silicate Melts Containing 17 mass% Al2O3 and 10 mass% MgO , 2012 .

[19]  T. Lam,et al.  Phase Equilibria in Synthetic Coal–Petcoke Slags (Al2O3–CaO–FeO–SiO2–V2O3) under Simulated Gasification Conditions , 2011 .

[20]  Fushen Li,et al.  Relation Between Viscosity and Electrical Conductivity of Silicate Melts , 2011 .

[21]  K. Chou,et al.  New method for viscosity estimation of slags in the CaO–FeO–MgO–MnO–SiO2 system using optical basicity , 2010 .

[22]  QifengShu,et al.  Viscosity estimation for slags containing calcium fluoride , 2005 .

[23]  H. S. Ray,et al.  Simple method for theoretical estimation of viscosity of oxide melts using optical basicity , 2004 .

[24]  R. R. Moskalyk,et al.  Processing of vanadium: a review , 2003 .

[25]  K. Mills.  The Influence of Structure on the Physico-chemical Properties of Slags. , 1993 .

[26]  M. Ingram,et al.  Comments on the application of optical basicity to glass , 1992 .

[27]  F. D. Richardson,et al.  The behaviour of sulphur in silicate and aluminate melts , 1954, Proceedings of the Royal Society of London. Series A. Mathematical and Physical Sciences.