论文信息 - Chalcogenide glass fiber with a core-cladding structure.

Chalcogenide glass fiber with a core-cladding structure.

GeAsSeTe, GeSeTeTl, and GeSeTe glass fibers with a core-cladding structure were prepared by one of two methods: crucible drawing or preform drawing. The diameter of the core was 340 microm and that of the cladding was 440 microm. The transmission loss spectra of the fibers were measured by the cut-back method. The crucible drawing method was preferable to reduce the loss due to structural imperfections at the interface of the core and cladding. The lowest loss of 1.7 dB/m was achieved at 10.6 microm (the wavelength of the CO(2) laser) in the fibers with a GeSeTe core and a GeAsSeTe cladding. Transmission of CO(2) laser power was examined using a 1.5-m long fiber and an output power of 2 W (2.2 kW/cm(2) in power density) was obtained.

[1] L. Tichý,et al. Influence of oxygen traces on physical properties of glassy GeSe2 , 1987 .

[2] S. Sato,et al. High-power CO laser transmission through As-S glass fibres , 1984 .

[3] Transmission loss of Ge-Se-Te and Ge-Se-Te-Tl glass fibers , 1987 .

[4] Tomoo Fujioka,et al. High power, high intensity CO infrared laser transmission through As2S3 glass fibers , 1986 .

[5] S. Sakuragi,et al. Infrared image guide with bundled As-S glass fibers. , 1985, Applied optics.

[6] Makoto Kikuchi,et al. CO Laser Power Delivery By As2S3 IR Glass Fiber With Teflon Cladding , 1986, Optics & Photonics.

[7] Toshiharu Yamashita,et al. Low‐loss chalcogenide glass fiber with core‐cladding structure , 1988 .

[8] A. Bornstein,et al. Chalcogenide infrared As2−xSe3+x glass fibers , 1985 .

[9] J. A. Savage,et al. The potential of Ge-As-Se-Te glasses as 3–5 μm and 8–12 μm infrared optical materials , 1980 .

[10] J. Nishii,et al. Oxide impurity absorptions in Ge-Se-Te glass fibres , 1989 .

[11] T. Katsuyama,et al. Low‐loss Te‐based chalcogenide glass optical fibers , 1986 .

[12] Paul Klocek,et al. Chalcogenide Glass Optical Fibers And Image Bundles: Properties And Applications , 1987 .

[13] Takashi Yamagishi,et al. Optical and thermal properties of chalcogenide Ge-As-Se-Te glasses for IR fibers , 1987 .