High strength nylon micro- and nanofiber based nonwovens via spunbonding

In this study we explore the feasibility of using of islands-in-the-sea (I/S) fibers in the spunbond process to produce relatively high strength micro- and nanofiber webs. The relationships between the number of islands, percent polymer composition, and the fiber and fabric properties are reported. Nylon 6 (N6) and poly (lactic) acid (PLA) were used as the islands and sea polymers, respectively. Micro- and nanofibers were obtained by dissolving PLA polymer from the final spunbond nonwovens. The fibers with 25% N6 showed a decrease in fiber diameter from 1.3 to 0.36 μm (micron) when the number of islands was increased from 36 to 360. The diameter of fibers with 75% N6 showed a decline from 2.3 to 0.5 μm for the same range. Hydroentangling was found to be the preferred method of bonding of the I/S structures; the bonded structures were able to withstand postprocessing steps required for dissolving of the sea from the resulting nonwovens. Hydroentanged micro- and nanofiber based nonwovens demonstrated high tensile and tear properties, which were insensitive to the N6 fiber size and its mechanical properties. Bonding efficiency and web uniformity were found to be dominant factors influencing the fabric performance. Overall, our study demonstrated that the I/S configuration is a promising technique for high speed and high throughput production of strong and light weight nonwovens comprised of micro- and nanofibers. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007

[1]  M. Takayanagi,et al.  Relationship between orientation of amorphous chains and modulus in highly oriented polypropylene , 1981 .

[2]  Takeshi Kikutani,et al.  High‐speed melt spinning of bicomponent fibers: Mechanism of fiber structure development in poly(ethylene terephthalate)/polypropylene system , 1996 .

[3]  Hiroshi Ito,et al.  Fine structure and physical properties of polyethylene/poly(ethylene terephthalate) bicomponent fibers in high-speed spinning. I. Polyethylene sheath/poly(ethylene terephthalate) core fibers , 2000 .

[4]  L. Wadsworth,et al.  Properties of PP/PET bicomponent melt blown microfiber nonwovens after heat-treatment , 2003 .

[5]  L. Wadsworth,et al.  Attenuating PP/PET bicomponent melt blown microfibers , 2003 .

[6]  Younan Xia,et al.  Electrospinning of nanofibers with core-sheath, hollow, or porous structures , 2005 .

[7]  R. Kessick,et al.  Microscale electrospinning of polymer nanofiber interconnections , 2003 .

[8]  Gajanan S. Bhat,et al.  Thermal bonding of polypropylene nonwovens: Effect of bonding variables on the structure and properties of the fabrics , 2004 .

[9]  Andreas Greiner,et al.  Compound Core–Shell Polymer Nanofibers by Co‐Electrospinning , 2003 .

[10]  R. W. Tock,et al.  Electrospinning of nanofibers , 2005 .

[11]  Gajanan S. Bhat,et al.  Extruded continuous filament nonwovens: Advances in scientific aspects , 2002 .

[12]  Sang Yong Kim,et al.  Effects of interface on the dynamic mechanical properties of PET/nylon 6 bicomponent fibers , 1999 .

[13]  S. Rwei,et al.  PBT/PET conjugated fibers: Melt spinning, fiber properties, and thermal bonding , 2004 .

[14]  D. Reneker,et al.  Nanometre diameter fibres of polymer, produced by electrospinning , 1996 .

[15]  A. T. Johnson,et al.  Electrostatically-generated nanofibers of electronic polymers , 2001 .

[16]  Y. Kimura,et al.  Preparing a Core-Sheath Bicomponent Fiber of Poly(butylene Terephthalate)/Poly(butylene Succinate-co-L-lactate) , 2000 .

[17]  Younan Xia,et al.  Electrospinning of Nanofibers: Reinventing the Wheel? , 2004 .

[18]  K. Koyama,et al.  Structure Formation of Blend and Sheath/Core Conjugated Fibers in High-Speed Spinning of PET, Including a Small Amount of PMMA , 2003 .