Optimising bioactive glass scaffolds for bone tissue engineering.

A 3D scaffold has been developed that has the potential to fulfil the criteria for an ideal scaffold for bone tissue engineering. Sol-gel derived bioactive glasses of the 70S30C (70 mol% SiO2, 30 mol% CaO) composition have been foamed to produce 3D bioactive scaffolds with hierarchical interconnected pore morphologies similar to trabecular bone. The scaffolds consist of a hierarchical pore network with macropores in excess of 500 microm connected by pore windows with diameters in excess of 100 microm, which is thought to be the minimum pore diameter required for tissue ingrowth and vasularisation in the human body. The scaffolds also have textural porosity in the mesopore range (10-20 nm). The scaffolds were sintered at 600, 700, 800 and 1000 degrees C. As sintering temperature was increased to 800 degrees C the compressive strength increased from 0.34 to 2.26 MPa due to a thickening of the pore walls and a reduction in the textural porosity. The compressive strength is in the range of that of trabecular bone (2-12 MPa). Importantly, the modal interconnected pore diameter (98 microm) was still suitable for tissue engineering applications and bioactivity is maintained. Bioactive glass foam scaffolds sintered at 800 degrees C for 2 h fulfill the criteria for an ideal scaffold for tissue engineering applications.

[1]  W. Hayes,et al.  Bone compressive strength: the influence of density and strain rate. , 1976, Science.

[2]  Larry L Hench,et al.  Third-Generation Biomedical Materials , 2002, Science.

[3]  B. Morrey,et al.  Twenty-five-Year Survivorship of Two Thousand Consecutive Primary Charnley Total Hip Replacements: Factors Affecting Survivorship of Acetabular and Femoral Components , 2002, The Journal of bone and joint surgery. American volume.

[4]  Julian R Jones,et al.  Factors affecting the structure and properties of bioactive foam scaffolds for tissue engineering. , 2004, Journal of biomedical materials research. Part B, Applied biomaterials.

[5]  E. Teller,et al.  On a Theory of the van der Waals Adsorption of Gases , 1940 .

[6]  Larry L. Hench,et al.  Crystallization kinetics of tape cast bioactive glass 45S5 , 2003 .

[7]  K. Sing.  Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Recommendations 1984) , 1985 .

[8]  Larry L. Hench,et al.  Bioceramics: From Concept to Clinic , 1991 .

[9]  Julian R Jones,et al.  Bioactive sol-gel foams for tissue repair. , 2002, Journal of biomedical materials research.

[10]  L. Hench,et al.  A gel-derived mesoporous silica reference material for surface analysis by gas sorption - 1. Textural features , 2000 .

[11]  P. Richet,et al.  High-temperature X-ray diffraction and Raman spectroscopy of diopside and pseudowollastonite , 1998 .

[12]  A I Caplan,et al.  Stem cell technology and bioceramics: from cell to gene engineering. , 1999, Journal of biomedical materials research.

[13]  A. Clark,et al.  Effect of Texture on the Rate of Hydroxyapatite Formation on Gel-Silica Surface , 1995 .

[14]  L L Hench,et al.  Gene-expression profiling of human osteoblasts following treatment with the ionic products of Bioglass 45S5 dissolution. , 2001, Journal of biomedical materials research.

[15]  K. Kurisu,et al.  In vivo histological changes occurring in hydroxyapatite cranial reconstruction--case report. , 2001, Neurologia medico-chirurgica.

[16]  L. Hench,et al.  Mesoporous calcium silicate glasses. I. Synthesis , 2003 .

[17]  M. Vallet‐Regí,et al.  Sol−Gel Glasses as Precursors of Bioactive Glass Ceramics , 2003 .

[18]  M. Ashby,et al.  Cellular solids: Structure & properties , 1988 .

[19]  T Kitsugi,et al.  Solutions able to reproduce in vivo surface-structure changes in bioactive glass-ceramic A-W. , 1990, Journal of Biomedical Materials Research.

[20]  S. Lowell,et al.  Theory of mercury porosimetry hysteresis , 1984 .

[21]  E. Barrett,et al.  (CONTRIBUTION FROM THE MULTIPLE FELLOWSHIP OF BAUGH AND SONS COMPANY, MELLOX INSTITUTE) The Determination of Pore Volume and Area Distributions in Porous Substances. I. Computations from Nitrogen Isotherms , 1951 .

[22]  J. Petrovic.  Review Mechanical properties of ice and snow , 2003 .

[23]  F. Kleitz,et al.  Evolution of mesoporous materials during the calcination process: structural and chemical behavior , 2001 .

[24]  Julian R. Jones,et al.  Effect of surfactant concentration and composition on the structure and properties of sol-gel-derived bioactive glass foam scaffolds for tissue engineering , 2003 .

[25]  Larry L. Hench,et al.  Biomedical materials for new millennium: perspective on the future , 2001 .

[26]  Lorna J. Gibson,et al.  Cellular materials as porous scaffolds for tissue engineering , 2001 .

[27]  Toshiaki Takezawa,et al.  A strategy for the development of tissue engineering scaffolds that regulate cell behavior. , 2003, Biomaterials.