Fast equilibration of silane/hydrogen plasmas in large area RF capacitive reactors monitored by optical emission spectroscopy

The optimal plasma parameters for plasma processing, such as deposition of microcrystalline silicon from silane and hydrogen, are generally chosen in steady-state discharge conditions. However, this steady state must be reached in a short time after plasma ignition to avoid significant film deposition in non-optimal conditions during the plasma transient phase.Simple and inexpensive time-resolved optical emission spectroscopy has been used to measure the plasma time evolution from ignition to steady-state conditions in a large area RF capacitive plasma reactor. Absolute values of silane and hydrogen molecular number densities, relative values of electron density, and qualitative information on electron temperature were obtained without the need for absolute intensity calibration. Apart from the experimental verification of constant electron temperature, the particular condition here is that the emission intensities should be followed from the instant of ignition, since the molecular densities are known at this instant.A plasma model for the reactor, and a dispersive axial flow model for the pumping line, were used to show why the plasma chemistry in a well-designed large area reactor generally reaches steady-state conditions in less than one second. The optimal design for fast equilibration is a closed, directly-pumped showerhead reactor with a uniform plasma which fills the whole reactor volume.

[1]  W. Schwarzenbach,et al.  Sheath impedance effects in very high frequency plasma experiments , 1996 .

[2]  M. Kondo,et al.  Gas temperature and surface heating in plasma enhanced chemical-vapour-deposition , 2006 .

[3]  John C. Slattery,et al.  Advanced transport phenomena , 1999 .

[4]  B. Rech,et al.  The role of plasma induced substrate heating during high rate deposition of microcrystalline silicon solar cells , 2006 .

[5]  L. Feitknecht,et al.  Plasma deposition of thin film silicon: kinetics monitored by optical emission spectroscopy , 2002 .

[6]  E. Katsia,et al.  High pressure regime of plasma enhanced deposition of microcrystalline silicon , 2005 .

[7]  F. Kampas,et al.  Origin of emitting species in the plasma deposition of a‐Si:H alloys , 1981 .

[8]  Bernd Rech,et al.  Deposition of highly efficient microcrystalline silicon solar cells under conditions of low H2 dilution: the role of the transient depletion induced incubation layer , 2007 .

[9]  A. Howling,et al.  A gas flow uniformity study in large-area showerhead reactors for RF plasma deposition , 2000 .

[10]  J. Perrin,et al.  Dissociation cross sections of silane and disilane by electron impact , 1982 .

[11]  A. Howling,et al.  Dust Particle Diagnostics in Rf Plasma Deposition of Silicon and Silicon Oxide Films (Invited) , 1998 .

[12]  Yukio Watanabe,et al.  Formation and behaviour of nano/micro-particles in low pressure plasmas , 2006 .

[13]  B. Rech,et al.  Transient depletion of source gases during materials processing: a case study on the plasma deposition of microcrystalline silicon , 2007 .

[14]  J. Perrin,et al.  Emission cross sections from fragments produced by electron impact on silane , 1982 .

[15]  A. Bouchoule,et al.  Particle generation and behavior in a silane‐argon low‐pressure discharge under continuous or pulsed radio‐frequency excitation , 1991 .

[16]  A. Howling,et al.  Optimization of the microcrystalline silicon deposition efficiency , 2007 .

[17]  A. Howling,et al.  Degree of dissociation measured by FTIR absorption spectroscopy applied to VHF silane plasmas , 1998 .

[18]  L. Feitknecht,et al.  Microcrystalline silicon deposited at high rate on large areas from pure silane with efficient gas utilization , 2007 .

[19]  A. Howling,et al.  Applications of the cavity ring-down technique to a large-area rf-plasma reactor , 1999 .

[20]  J. Schmitt,et al.  Probe measurements of plasma potential nonuniformity due to edge asymmetry in large-area radio-frequency reactors: The telegraph effect , 2005 .

[21]  J. Perrin,et al.  The physics of plasma-enhanced chemical vapour deposition for large-area coating: industrial application to flat panel displays and solar cells , 2000 .

[22]  Meifang Zhu,et al.  High quality microcrystalline Si films by hydrogen dilution profile , 2006 .

[23]  A. Howling,et al.  TIME-RESOLVED MEASUREMENTS OF HIGHLY POLYMERIZED NEGATIVE IONS IN RADIO FREQUENCY SILANE PLASMA DEPOSITION EXPERIMENTS , 1994 .

[24]  U. Fantz,et al.  Spectroscopic diagnostics and modelling of silane microwave plasmas , 1998 .

[25]  O. Leroy,et al.  Cross-Sections, Rate Constants and Transport Coefficients in Silane Plasma Chemistry , 1996 .

[26]  Eva Stoffels,et al.  Electron density fluctuations in a dusty Ar/SiH4 rf discharge , 1995 .

[27]  A. Howling,et al.  Plasma silane concentration as a determining factor for the transition from amorphous to microcrystalline silicon in SiH4/H2 discharges , 2007 .

[28]  W. Stoffels,et al.  Temperature dependence and silane consumption during particle formation in Ar-silane RF capacitively coupled plasma , 2004, IEEE Transactions on Plasma Science.

[29]  B. Rech,et al.  Microcrystalline silicon deposition: Process stability and process control , 2007 .

[30]  J. Perrin,et al.  Two-dimensional modelling of - radio-frequency discharges for a-Si:H deposition , 1998 .

[31]  Bernard Drevillon,et al.  Substrate selectivity in the formation of microcrystalline silicon: Mechanisms and technological consequences , 1995 .

[32]  B. Rech,et al.  Highly efficient microcrystalline silicon solar cells deposited from a pure SiH4 flow , 2005 .