Zirconia Nanoparticles Made in Spray Flames at High Production Rates

Synthesis of zirconia nanoparticles by flame spray pyrolysis (FSP) at high production rates is investigated. Product powder is collected continuously in a baghouse filter unit that is cleaned periodically by air-pressure shocks. Nitrogen adsorption (BET), X-ray diffractometry (XRD), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA) are used to characterize the product powder. The effect of powder production rate (up to 600 g/h), dispersion gas flow rate, and precursor concentration on product particle size, crystallinity, morphology, and purity is investigated. The primary particle size of zirconia is controlled from 6 to 35 nm, while the crystal structure consists of mostly tetragonal phase (80-95 wt%), with the balance monoclinic phase at all process conditions. The tetragonal crystal size is close to the primary particle size, which indicates weak agglomeration of single crystals.

[1]  Gary L. Messing,et al.  Ceramic Powder Synthesis by Spray Pyrolysis , 1993 .

[2]  Lutz Mädler,et al.  Controlled synthesis of nanostructured particles by flame spray pyrolysis , 2002 .

[3]  S. Ramasamy,et al.  X-ray diffraction study of phase transformation in hydrolyzed zirconia nanoparticles , 1999 .

[4]  S. Pratsinis,et al.  OH Surface Density of SiO 2 and TiO 2 by Thermogravimetric Analysis , 2003 .

[5]  Sotiris E. Pratsinis,et al.  Synthesis of silica‐carbon particles in a turbulent H2‐air flame aerosol reactor , 2001 .

[6]  W. Stark,et al.  Flame-made ceria nanoparticles , 2002 .

[7]  H. Gleiter,et al.  Materials with ultrafine microstructures: Retrospectives and perspectives , 1992 .

[8]  M. Mayo,et al.  Surface chemistry effects on the processing and superplastic properties of nanocrystalline oxide ceramics , 1999 .

[9]  T. Morse,et al.  A Novel Aerosol Combustion Process for the High Rate Formation of Nanoscale Oxide Particles , 2001 .

[10]  R. W. Cheary,et al.  Axial Divergence in a Conventional X-ray Powder Diffractometer. I. Theoretical Foundations , 1998 .

[11]  R. W. Cheary,et al.  A fundamental parameters approach to X-ray line-profile fitting , 1992 .

[12]  Maurice Gell,et al.  Application opportunities for nanostructured materials and coatings , 1995 .

[13]  C. Berndt,et al.  On the size-dependent phase transformation in nanoparticulate zirconia , 2000 .

[14]  C. H. Chen,et al.  Preparation of zirconia and yttria-stabilized zirconia (YSZ) fine powders by flame-assisted ultrasonic spray pyrolysis (FAUSP) , 1998 .

[15]  R. Garvie.  THE OCCURRENCE OF METASTABLE TETRAGONAL ZIRCONIA AS A CRYSTALLITE SIZE EFFECT , 1965 .

[16]  J. Helble,et al.  Morphological Control of Zirconia Nanoparticles through Combustion Aerosol Synthesis , 2004 .

[17]  L. Mädler,et al.  Bismuth Oxide Nanoparticles by Flame Spray Pyrolysis , 2004 .

[18]  Sotiris E. Pratsinis,et al.  Flame aerosol synthesis of ceramic powders , 1998 .

[19]  W. Hartmann,et al.  Fumed oxides as base materials for ceramic applications , 1989 .

[20]  Lutz Mädler,et al.  Flame synthesis of nanoparticles , 2001 .

[21]  Christopher C. Berndt,et al.  Nanomaterial powders and deposits prepared by flame spray processing of liquid precursors , 1997 .

[22]  Lutz Mädler,et al.  Nanoparticle synthesis at high production rates by flame spray pyrolysis , 2003 .

[23]  S. Pratsinis,et al.  Self-preserving size distributions of agglomerates , 1995 .