Micro-crack behavior of carbon fiber reinforced thermoplastic modified epoxy composites for cryogenic applications

Three different types of thermoplastics, poly(ether imide) (PEI), polycarbonate (PC), and poly(butylene terephthalate) (PBT) were used to modify epoxy for cryogenic applications. Carbon fiber reinforced thermoplastic modified epoxy composites were also prepared through vacuum-assisted resin transfer molding (RTM). Dynamic mechanical analysis (DMA) shows that the storage moduli of PEI, PC, and PBT modified epoxies are 30%, 21%, and 17% higher than that of the neat epoxy respectively. The impact strength of the modified epoxies at cryogenic temperature increases with increasing thermoplastic content up to 1.5 wt.% and then decreases for further loading (2.0 wt.%). The coefficient of thermal expansion (CTE) values of the PBT, PEI, and PC modified epoxies also decreased by 17.76%, 25.42%, and 30.15%, respectively, as compared with that of the neat epoxy. Optical microscopy image analysis suggests that the presence of PEI and PC in the carbon fiber reinforced epoxy composites can prevent the formation of micro-cracks. Therefore, both the PEI and PC were very effective in preventing micro-crack formation in the composites during thermal cycles at cryogenic condition due to their low CTE values and high impact strength.

[1]  Jang‐Kyo Kim,et al.  Fatigue damage behaviors of carbon fiber-reinforced epoxy composites containing nanoclay , 2010 .

[2]  Yonggang Huang,et al.  Reinforcement of epoxy resins with multi-walled carbon nanotubes for enhancing cryogenic mechanical properties , 2009 .

[3]  F. Chang,et al.  Reactive compatibilization of polyamide‐6 (PA 6)/polybutylene terephthalate (PBT) blends by a multifunctional epoxy resin , 2000 .

[4]  C. Ha,et al.  Influence of processing method on the fracture toughness of thermoplastic-modified, carbon-fiber-reinforced epoxy composites , 1999 .

[5]  B. Sankar,et al.  Gas permeability of various graphite/epoxy composite laminates for cryogenic storage systems , 2008 .

[6]  Joung-Man Park,et al.  Interfacial adhesion and microfailure modes of electrodeposited carbon fiber/epoxy-PEI composites by microdroplet and surface wettability tests. , 2002, Journal of colloid and interface science.

[7]  M. C. Chen,et al.  Miscibility and fracture behaviour of an epoxy resin-bisphenol-a polycarbonate blend , 1992 .

[8]  Jesús Rodríguez,et al.  Fracture properties of epoxy/poly(styrene-co-allylalcohol) blends , 2007 .

[9]  Y. Mai,et al.  On toughness and stiffness of poly(butylene terephthalate) with epoxide-containing elastomer by reactive extrusion , 2004 .

[10]  V. T. Bui,et al.  Modification of high‐performance polymer composite through high‐energy radiation and low‐pressure plasma for aerospace and space applications , 2006 .

[11]  T. Takeda,et al.  Deformation and progressive failure behavior of woven-fabric-reinforced glass/epoxy composite laminates under tensile loading at cryogenic temperatures , 2005 .

[12]  Xiaosu Yi,et al.  Cure-induced phase separation of epoxy/DDS/PEK-C composites and its temperature dependency , 2008 .

[13]  J. Szczerba,et al.  Mechanical properties of epoxy resin modified with polycarbonate and reactive polybutadiene , 2007 .

[14]  M. M. El-Tonsy,et al.  Automatic measurement of the absolute CTE of thin polymer samples: I-Effect of multiple processing on thermal expansion of polypropylene films , 2004 .

[15]  S. Zhang,et al.  Inhomogeneous toughening of carbon fiber/epoxy composite using electrospun polysulfone nanofibrous membranes by in situ phase separation , 2008 .

[16]  I. Partridge,et al.  Heterogeneous phase separation around fibres in epoxy/PEI blends and its effect on composite delamination resistance , 1997 .

[17]  Xiaoyun Liu,et al.  Kinetics of phase separation at the early stage of spinodal decomposition in epoxy resin modified with PEI blends , 2009 .

[18]  S. Priya,et al.  Studies on the Mechanical Performance of PMMA Toughened Epoxy–Silk and PC Toughened Epoxy–Silk Fabric Composites , 2005 .

[19]  Jun Sun,et al.  Mechanical properties of an epoxy resin toughened by polyester , 2003 .

[20]  Willie E. Rochefort,et al.  Studies on the thermal stability and degradation kinetics of Pd/PC nanocomposites , 2010 .

[21]  M. C. Chen,et al.  Miscibility and fracture behaviour of epoxy resin-nitrated polyetherimide blends , 1995 .

[22]  R. Thiruvengadathan,et al.  Preparation and characterization of a double filler polymeric nanocomposite , 2007 .

[23]  J. Seferis,et al.  Influence of elastomer distribution on the cryogenic microcracking of carbon fiber/epoxy composites , 2003 .

[24]  A. S. Luyt,et al.  Chemical Resistance, Void Contents, and Morphological Properties of Hildegardia Fabric/Polycarbonate-Toughened Epoxy Composites , 2007 .

[25]  D. J. Hourston,et al.  Toughening of epoxy resins with thermoplastics : 3. An investigation into the effects of composition on the properties of epoxy resin blends , 1997 .

[26]  Ben Wang,et al.  Effect of Nanotube Functionalization on the Coefficient of Thermal Expansion of Nanocomposites , 2007 .

[27]  J. Seferis,et al.  Nanoclay reinforcement effects on the cryogenic microcracking of carbon fiber/epoxy composites , 2002 .

[28]  A. Ghosh,et al.  Crystallization kinetics and morphological behavior of reactively processed PBT/epoxy blends , 2003 .

[29]  J. Suhr,et al.  Experimental and analytical investigation of mechanical damping and CTE of both SiO2 particle and carbon nanofiber reinforced hybrid epoxy composites , 2011 .

[30]  T. Sınmazçelik,et al.  Thermal cycles effects on interlaminar shear strength (ILSS) and impact behaviour of carbon/PEI composites , 2006 .

[31]  R. P. Reed,et al.  Cryogenic composite supports: a review of strap and strut properties , 1997 .

[32]  Brent Hamilton,et al.  Upper Stage Flight Experiment (USFE) Integral Structure Development Effort , 2004 .