Oxidation resistance and hardness of TiAlSiN/CrAlYN multilayer films deposited by the arc ion plating method

Abstract Multilayered TiAlSiN/CrAlYN films were synthesized on cemented carbide, silicon and SUS304 substrates with various periods and investigated their oxidation resistance and hardness. The multilayer period between 5.6 nm and 23.2 nm was obtained by controlling the rotation speed of the substrates. X-ray diffraction patterns showed that the TiAlSiN/CrAlYN multilayer films after annealed at 1000 °C for 1 h retained the nitride structure and no peaks indicating metal oxide were observed for the films. Using the glow discharge optical emission spectrometry depth profiling method, an oxidation peak was only observed around the film surface. Hardness of TiAlSiN/CrAlYN multilayer films was measured using a conventional micro-Vickers hardness tester and the result showed that it changed depending on the multilayer period. That is, the film with a period of 8.7 nm exhibited the highest hardness with 37.1 GPa, which was higher than the value calculated based on the rule of mixtures of TiAlSiN monolayer and CrAlYN monolayer.

[1]  P. Yashar,et al.  Structure and mechanical properties of polycrystalline CrN/TiN superlattices , 1998 .

[2]  X. Qu,et al.  High-temperature oxidation behavior of TiAl-based alloys fabricated by spark plasma sintering , 2009 .

[3]  P. Mayrhofer,et al.  Impact of yttrium on structure and mechanical properties of Cr–Al–N thin films , 2007 .

[4]  S. Barnett,et al.  Growth of single-crystal TiN/VN strained-layer superlattices with extremely high mechanical hardness , 1987 .

[5]  M. Gu,et al.  Coherent growth and mechanical properties of AlN/VN multilayers , 2004 .

[6]  Y. Yamada,et al.  Structure and properties of Al–Ti–Si–N coatings prepared by the cathodic arc ion plating method for high speed cutting applications , 2001 .

[7]  T. Nomura,et al.  Formation of cubic-A1N in TiN/A1N superlattice , 1996 .

[8]  P. Zeman,et al.  Hard amorphous nanocomposite coatings with oxidation resistance above 1000°C , 2008 .

[9]  O. Knotek,et al.  Properties of arc-evaporated CrN and (Cr, Al)N coatings , 1991 .

[10]  S. Vepřek,et al.  Avoiding the high-temperature decomposition and softening of (Al1−xTix)N coatings by the formation of stable superhard nc-(Al1−xTix)N/a-Si3N4 nanocomposite , 2004 .

[11]  J. Schneider,et al.  The effect of yttrium incorporation on the oxidation resistance of Cr–Al–N coatings , 2008 .

[12]  W. Münz.  Titanium aluminum nitride films: A new alternative to TiN coatings , 1986 .

[13]  Kenji Yamamoto,et al.  Effects of bilayer thickness and post-deposition annealing on the mechanical and structural properties of (Ti,Cr,Al)N/(Al,Si)N multilayer coatings , 2009 .

[14]  H. Barshilia,et al.  Structure and properties of reactive DC magnetron sputtered TiN/NbN hard superlattices , 2004 .

[15]  Tetsuya Suzuki,et al.  Microhardness and lattice parameter of Cr1−xAlxN films , 2002 .

[16]  L. Hultman,et al.  Growth, structure, and microhardness of epitaxial TiN/NbN superlattices , 1992 .

[17]  P. Zeman,et al.  Hard a-Si3N4/MeNx Nanocomposite Coatings with High Thermal Stability and High Oxidation Resistance , 2007 .