Plasma-sprayed "HA" coatings on commercial orthopedic and dental implants consist of mixtures of calcium phosphate phases, predominantly a crystalline calcium phosphate phase, hydroxyapatite (HA) and an amorphous calcium phosphate (ACP) with varying HA/ACP ratios. Alternatives to the plasma-spray method are being explored because of some of its disadvantages. The purpose of this study was to deposit an adherent apatite coating on titanium substrate using a two-step method. First, titanium substrates were immersed in acidic solution of calcium phosphate resulting in the deposition of a monetite (CaHPO4) coating. Second, the monetite crystals were transformed to apatite by hydrolysis in NaOH solution. Composition and morphology of the initial and final coatings were identified using X-ray diffraction (XRD), Scanning Electron Microscopy, and Energy Dispersive Spectroscopy (EDS). The final coating was porous and the apatite crystals were agglomerated and followed the outline of the large monetite crystals. EDS revealed the presence of calcium and phosphorous elements on the titanium substrate after removing the coating using tensile or scratching tests. The average tensile bond of the coating was 5.2 MPa and cohesion failures were observed more frequently than adhesion failures. The coating adhesion measured using scratch test with a 200-microm-radius stylus was 13.1N. Images from the scratch tracks demonstrated that the coating materials were squashed without fracturing inside and/or at the border of the tracks until the failure point of the coating. In conclusion, this study showed the potential of a chemical deposition method for depositing a coating consisting of either monetite or apatite. This method has the advantage of producing a coating with homogenous composition on even implants of complex geometry or porosity. This method involves low temperatures and, therefore, can allow the incorporation of growth factors or biogenic molecules.
[1]
Yasuhiro Fukui,et al.
A functionally graded titanium/hydroxyapatite film obtained by sputtering
,
2002,
Journal of materials science. Materials in medicine.
[2]
Y. Yokogawa,et al.
Bond strength improvement of hydroxyapatite/titanium composite coating by partial nitriding during RF-thermal plasma spraying
,
2003
.
[3]
Claude Martelet,et al.
Relationship between surface properties (roughness, wettability) of titanium and titanium alloys and cell behaviour
,
2003
.
[4]
R. Legeros.
The unit-cell dimensions of human enamel apatite: effect of chloride incorporation.
,
1975,
Archives of oral biology.