Luminescence induced by elastic deformation of ZnS:Mn nanoparticles

Abstract When the thin film of ZnS:Mn nanoparticles deposited on a glass substrate is elastically deformed by applying a load, then initially the mechanoluminescence (ML) intensity increases with time, attains a peak value Im at a particular time tm, and later on it decreases with time. The rise and decay characteristics of the ML produced during release of the load are also similar to those produced during the application of load. Similar rise, occurrence of peak and then decrease in ML intensity are also found, when the film is deformed impulsively by dropping a steel ball of small mass from a low height; however, in this case, the time durations for the occurrence of ML and decay time of ML are very short. In the cases of loading and impulsive deformation ,after tm, initially the ML intensity decreases at a fast rate and then at a slow rate, in which the decay time of fast decrease is equal to the time-constant for rise of pressure and the decay time for slow decrease is equal to the relaxation time of the surface charges. In the case of loading, the peak intensity Im and the total intensity IT of ML increase quadratically with the magnitude of applied pressure; however, in the case of impulsive deformation, both the Im and IT increase linearly with the height through which the ball is dropped on to the sample. In the case of deformation of the samples at a fixed strain rate, Im should increase linearly with the applied pressure. The elastico ML in ZnS:Mn nanoparticles can be understood on the basis of the piezoelectrically-induced electron detrapping model, in which the local piezoelectric field near the Mn2+ centres reduces the trap-depth, and therefore, the detrapping of filled electron traps takes place, and subsequently the energy released non-radiatively during the electron–hole recombination excites the Mn2+ centres and de-excitation gives rise to the ML. The equal number of photons emitted during the application of pressure, release of pressure, and during the successive applications of pressure, indicates that the detrapped electron-traps get filled during the relaxation of the surface charges induced by the application and release of pressure because the charge carriers move to reduce the surface charges. On the basis of the piezoelectrically-induced electron detrapping model, expressions are derived for different characteristics of the ML of ZnS:Mn nanoparticles and a good agreement is found between the theoretical and experimental results. The expressions explored for the dependence of ML intensity on several parameters may be useful in tailoring the suitable nanomaterials capable of exhibiting ML during their elastic deformation. The values of the relaxation time of surface charges, time-constant for the rise of pressure, and the threshold pressure can be determined from the measurement of the time-dependence of ML. It seems that the trapping and detrapping of charge carriers in materials can be studied using ML.

[1]  K. Nonaka,et al.  Visualization of stress distribution using mechanoluminescence from Sr3Al2O6: Eu and the nature of the luminescence mechanism , 1999 .

[2]  Weiyi Jia,et al.  Stress-induced mechanoluminescence in SrAl2O4:Eu2+,Dy3+ , 2006 .

[3]  P. Ferreira,et al.  On the nucleation of partial dislocations in nanoparticles , 2008 .

[4]  L. Sodomka The form of the pressure and luminescence brightness during impact on a luminescent layer , 1964 .

[5]  R. Bhargava,et al.  Doped nanocrystals of semiconductors - a new class of luminescent materials , 1994 .

[6]  S. Chu,et al.  The mechanism and characteristics of ZnS-based phosphor powders , 2004 .

[7]  V. F. Petrenko,et al.  Properties of II–VI semiconductors associated with moving dislocations , 1986 .

[8]  K. Sohn,et al.  Visualization of fractures in alumina ceramics by mechanoluminescence , 2005 .

[9]  A. Laha,et al.  Analysis of leakage current conduction phenomenon in thin SrBi2Ta2O9 films grown by excimer laser ablation , 2002 .

[10]  V. Bulović,et al.  Alternating current driven electroluminescence from ZnSe/ZnS:Mn/ZnS nanocrystals. , 2009, Nano letters.

[11]  M. Abdulkhadar,et al.  Elastic properties of consolidated nano-particles of ZnS and CdS , 1995 .

[12]  Banfield,et al.  Imperfect oriented attachment: dislocation generation in defect-free nanocrystals , 1998, Science.

[13]  Chao‐Nan Xu,et al.  Development of Elastico-Luminescent Nanoparticles and their Applications , 2006 .

[14]  Gallagher,et al.  Optical properties of manganese-doped nanocrystals of ZnS. , 1994, Physical review letters.

[15]  D. R. Vij,et al.  Luminescence of solids , 1998 .

[16]  P. Indovina,et al.  TEMPERATURE DEPENDENCE OF H/sub c3//H/sub c2/ NEAR T/sub c/ FOR Nb. , 1971 .

[17]  P. Tománek,et al.  Near‐field measurement of ZnS:Mn nanocrystal and bulk thin‐film electroluminescent devices , 2008, Journal of microscopy.

[18]  Chao-Nan Xu,et al.  Direct view of stress distribution in solid by mechanoluminescence , 1999 .

[19]  I. Chudáček The kinetics of the triboluminescence of zinc sulphide I , 1967 .

[20]  X. Tan,et al.  Size-induced strain and stiffness of nanocrystals , 2006 .

[21]  D. R. Reddy,et al.  Laser-like mechanoluminescence in ZnMnTe-diluted magnetic semiconductor , 2002 .

[22]  K. Nonaka,et al.  Electrical power generation characteristics of PZT piezoelectric ceramics , 1998, IEEE Transactions on Ultrasonics, Ferroelectrics and Frequency Control.

[23]  K. Sohn,et al.  Direct observation of crack tip stress field using the mechanoluminescence of SrAl2O4:(Eu, Dy, Nd) , 2004 .

[24]  J. Banfield,et al.  Water-driven structure transformation in nanoparticles at room temperature , 2003, Nature.

[25]  Chao-Nan Xu,et al.  Preparation and characteristics of highly triboluminescent ZnS film , 1999 .

[26]  S. R. Vadera,et al.  Multicolor electroluminescent devices using doped ZnS nanocrystals , 2004 .

[27]  Chao-Nan Xu,et al.  Artificial skin to sense mechanical stress by visible light emission , 1999 .

[28]  Chao‐Nan Xu,et al.  Triboluminescence of ZnS:Mn Films Deposited on Quartz Substrates with ZnO Buffer Layers , 2002 .

[29]  R. Mach,et al.  Physical Concepts of High‐Field, Thin‐Film Electroluminescence Devices , 1982 .

[30]  Kee-Sun Sohn,et al.  Mechanoluminescent SrAl2O4:Eu,Dy phosphor for use in visualization of quasidynamic crack propagation , 2007 .

[31]  B. P. Chandra,et al.  Strong mechanoluminescence induced by elastic deformation of rare-earth-doped strontium aluminate phosphors , 2009 .

[32]  I. C. Sage,et al.  Triboluminescent materials for structural damage monitoring , 2001 .

[33]  Chao-Nan Xu,et al.  Dynamic visualization of stress distribution by mechanoluminescence image , 2000 .

[34]  Csaba Szeles,et al.  Investigation of the electronic properties of cadmium zinc telluride surfaces using pulsed laser microwave cavity perturbation , 2001, SPIE Optics + Photonics.

[35]  J. Tomas,et al.  Mechanoluminescence of quartz particles during grinding in a stirred media mill , 2004 .

[36]  K. Sohn,et al.  Detection of Crack Propagation in Alumina Using SrAl2O4:(Eu,Dy) Luminescent Paint , 2007 .

[37]  B. P. Chandra Luminescence induced by moving dislocations in crystals , 1996 .

[38]  M. Schwartz Encyclopedia of smart materials , 2002 .

[39]  B. P. Chandra Mechanoluminescence induced by elastic deformation of coloured alkali halide crystals using pressure steps , 2008 .

[40]  I. C. Sage,et al.  Getting light through black composites: embedded triboluminescent structural damage sensors , 2001 .

[41]  B. P. Chandra,et al.  Classification of Mechanoluminescence , 1995 .

[42]  R. Scarmozzino Effects of hydrostatic pressure on triboluminescent materials , 1971 .

[43]  Chao-Nan Xu,et al.  Enhancement of adhesion and triboluminescence of ZnS:Mn films by annealing technique , 1999 .

[44]  B. P. Chandra,et al.  Characteristics of a.c. electroluminescence in thin film ZnS : Mn display devices , 2004 .