Dry-Spun Neat Cellulose Nanofibril Filaments: Influence of Drying Temperature and Nanofibril Structure on Filament Properties

Cellulose nanofibrils (CNF) were spun into filaments directly from suspension without the aid of solvents. The influence of starting material properties and drying temperature on the properties of filaments produced from three different CNF suspensions was studied. Refiner-produced CNF was ground using a microgrinder at grinding times of 50 and 100 minutes. Filament spinning was performed using a syringe pump-heat gun setting at three drying temperatures of 210 ◦C, 320 ◦C and 430 ◦C. The structure of starting CNF materials was first evaluated using a combination of optical and atomic force microscopy (AFM) techniques. Surface free energy analysis and attenuated total reflectance—Fourier transform infrared spectroscopy (ATR–FTIR) were used to study changes in hydrophobicity due to grinding. Morphology of the filaments was studied using SEM micrographs. The influence of different drying temperatures and grinding times on mechanical properties of the CNF filaments were further investigated through tensile tests and results were compared using statistical analysis .It was observed that drying temperature did not significantly influence the tensile properties of the filaments while cellulose nanofiber suspension type (grinding time) had a significant influence and improved mechanical properties. FTIR results confirmed an increase in crystallinity index and decrease in hydroxyl group availability due to grinding.

[1]  D. Gardner,et al.  Preparation and property assessment of neat lignocellulose nanofibrils (LCNF) and their composite films , 2017, Cellulose.

[2]  H. Orelma,et al.  High velocity dry spinning of nanofibrillated cellulose (CNF) filaments on an adhesion controlled surface with low friction , 2016, Cellulose.

[3]  A. Papageorgiou,et al.  Strength and Water Interactions of Cellulose I Filaments Wet-Spun from Cellulose Nanofibril Hydrogels , 2016, Scientific Reports.

[4]  E. Abraham,et al.  Nanocellulose, a tiny fiber with huge applications. , 2016, Current opinion in biotechnology.

[5]  K. Oksman,et al.  Dry-Spun Single-Filament Fibers Comprising Solely Cellulose Nanofibers from Bioresidue. , 2015, ACS applied materials & interfaces.

[6]  M. Poletto,et al.  Native Cellulose: Structure, Characterization and Thermal Properties , 2014, Materials.

[7]  L. Daniel Söderberg,et al.  Hydrodynamic alignment and assembly of nanofibrils resulting in strong cellulose filaments , 2014, Nature Communications.

[8]  P. Samyn.  Wetting and hydrophobic modification of cellulose surfaces for paper applications , 2013, Journal of Materials Science.

[9]  Alain Dufresne,et al.  Nanocellulose: a new ageless bionanomaterial , 2013 .

[10]  Alain Dufresne,et al.  Nanocellulose: From Nature to High Performance Tailored Materials , 2012 .

[11]  Ø. Gregersen,et al.  TEMPO-oxidized cellulose nanofiber films: effect of surface morphology on water resistance , 2012, Cellulose.

[12]  G. Huber,et al.  Simulating infrared spectra and hydrogen bonding in cellulose Iβ at elevated temperatures. , 2011, The Journal of chemical physics.

[13]  Jaakko V. I. Timonen,et al.  Multifunctional High‐Performance Biofibers Based on Wet‐Extrusion of Renewable Native Cellulose Nanofibrils , 2011, Advanced materials.

[14]  Ashlie Martini,et al.  Cellulose nanomaterials review: structure, properties and nanocomposites. , 2011, Chemical Society reviews.

[15]  T. Iwata,et al.  Structure and mechanical properties of wet-spun fibers made from natural cellulose nanofibers. , 2011, Biomacromolecules.

[16]  Siqun Wang,et al.  Novel Process for Isolating Fibrils from Cellulose Fibers by High-Intensity Ultrasonication. II. Fibril Characterization , 2010 .

[17]  K. Poduska,et al.  Roughness effects on contact angle measurements , 2008 .

[18]  Dong Il Yoo,et al.  FTIR analysis of cellulose treated with sodium hydroxide and carbon dioxide. , 2005, Carbohydrate research.

[19]  Tetsuo Kondo,et al.  FT-IR Microscopic Analysis of Changing Cellulose Crystalline Structure during Wood Cell Wall Formation , 1998 .

[20]  D. K. Owens,et al.  Estimation of the surface free energy of polymers , 1969 .