Transparent conducting CuCr1-xMgxO2 films prepared by pulsed laser deposition

Transparent conducting CuCr1-xMgxO2 thin films were prepared by pulsed laser deposition (PLD) from polycrystalline CuCr1-xMgxO2 targets. The derived CuCr1-xMgxO2 films were highly c-axis oriented deposited at higher substrate temperature. The micro structural, electrical as well as optical properties were studied. It was found that the films were relatively smooth, and behaved as semiconductors. The transmittances of the films in the visible region are about 80% with direct band gaps about 3.15eV. The results suggested that CuCr1-xMgxO2 films could be successfully prepared by PLD, which can broaden the applications of the transparent conducting oxides films.

[1] Shinzo Takata,et al. Transparent conducting p-type NiO thin films prepared by magnetron sputtering , 1993 .

[2] Weiwei Dong,et al. Synthesis of CuAlO2 ceramics using sol-gel , 2007 .

[3] David P. Cann,et al. Crystal chemistry and electrical properties of the delafossite structure , 2006 .

[4] Kalyan Kumar Chattopadhyay,et al. Synthesis and characterization of p-type transparent conducting CuAlO2 thin film by DC sputtering , 2003 .

[5] T. Minami. Transparent conducting oxide semiconductors for transparent electrodes , 2005 .

[6] Masayoshi Ohashi,et al. Preparation of CuAlO2 Films by Wet Chemical Synthesis. , 2002 .

[7] Bangchuan Zhao,et al. Fabrication of La0.8Na0.2Mn1−xCuxO3 (x = 0, 0.05) thin films on YSZ substrates via chemical solution deposition , 2004 .

[8] Kalyan Kumar Chattopadhyay,et al. Recent developments in the emerging field of crystalline p-type transparent conducting oxide thin films , 2005 .

[9] Janet Tate,et al. p-type conductivity in CuCr1−xMgxO2 films and powders , 2001 .

[10] Hideo Hosono,et al. P-type electrical conduction in transparent thin films of CuAlO2 , 1997, Nature.

[11] Tao Wang,et al. Electrical, optical and structural properties of CuCrO2 films prepared by pulsed laser deposition , 2007 .

[12] Tetsuji Okuda,et al. Magnetic, transport, and thermoelectric properties of the delafossite oxidesCuCr1−xMgxO2(0⩽x⩽0.04) , 2005 .