论文信息 - CORRIGENDUM: An x-ray diffraction examination of the FeTi-H2 system

CORRIGENDUM: An x-ray diffraction examination of the FeTi-H2 system

The alpha , beta 1, beta 2, and gamma phases exhibited by the FeTi-H2 system are shown to be isostructural with the corresponding phases of the FeTi-D2 system. Evidence is presented suggesting that the phases exhibited by a given FeTiHx specimen depend not only upon the hydrogen content but also upon the sample history and the method of preparation.

J. Lynch | J. Reilly | F. Reidinger

[1] J. Goldstone,et al. Optic modes in FeTiH1.14 , 1981 .

[2] W. Schäfer,et al. Transmission electron microscopy and neutron diffraction studies of Feti-H(D)☆ , 1980 .

[3] E. L. Huston,et al. Kinetic and dynamic aspects of rechargeable metal hydrides , 1980 .

[4] J. R. Johnson,et al. Lattice expansion as a measure of surface segregation and the solubility of hydrogen in α-FeTiHx , 1980 .

[5] B. Lengeler,et al. Compton profiles of FeTi and β-phase FeTi hydride , 1980 .

[6] H. Wenzl,et al. The specific heat of iron titanium hydride at room temperature , 1980 .

[7] J. M. Hastings,et al. Neutron diffraction study of α-iron titanium deuteride , 1980 .

[8] L. Schlapbach,et al. Structural phase transitions of FeTi-deuterides , 1979 .

[9] J. M. Hastings,et al. Neutron diffraction study of gamma iron titanium deuteride , 1979 .

[10] T. Schober. The iron-titanium - hydrogen system: A transmission electron microscope (TEM) study , 1979 .

[11] J. M. Hastings,et al. Neutron diffraction study of β iron titanium deuteride , 1978 .

[12] A. Attalla,et al. NMR studies of structure and diffusion in metal hydrides , 1977 .

[13] J. Reilly,et al. Formation and properties of iron titanium hydride , 1974 .