Impedance study on calcium nitrite as a penetrating corrosion inhibitor for steel in concrete

Abstract Penetrating corrosion inhibitors are thought to be able to penetrate through the capillary structure of concrete to reinforcing steel and to reduce the already initiated corrosion of steel. In this work the ability of calcium nitrite to inhibit the chloride induced corrosion of steel was studied. The test protocol was adjusted to simulate the performance of penetrating corrosion inhibitors in concrete structures. Steel samples were first prepassivated in saturated solution of Ca(OH) 2 and then exposed to the same solution with 1% NaCl addition, simulating pore liquid in chloride contaminated concrete. After the initiation of steel corrosion, the first dose of calcium nitrite was added, and then its concentration was gradually increased and the inhibition effect was related to the molar ratio of chloride to nitrite ions [Cl − ]/[NO 2 − ]. Different rates of the increase in the inhibitor concentration were applied. Electrochemical impedance spectroscopy was used to follow the behaviour of steel at different stages of the corrosion process. The evolution of acquired spectra reflected the initiation of localized corrosion of steel and then the gradual inhibition with increasing concentration of the inhibitor. It was found, that calcium nitrite is able to inhibit the initiated corrosion (pitting) of steel and the optimum inhibitor efficiency was observed for the [Cl − ]/[NO 2 − ] ratio below 1. The inhibition efficiency was larger, when this value of the [Cl − ]/[NO 2 − ] ratio was reached in early stages of the corrosion development. Calcium nitrite can be effective as a penetrating corrosion inhibitor for steel in concrete, if it will be present in the sufficient concentration at the steel surface in early stages of the corrosion development.

[1]  Carolyn M. Hansson,et al.  Corrosion inhibitors in concrete: Part III. Effect on time to chloride-induced corrosion initiation and subsequent corrosion rates of steel in mortar , 2001 .

[2]  K. Y. Ann,et al.  Effect of calcium nitrite-based corrosion inhibitor in preventing corrosion of embedded steel in concrete , 2006 .

[3]  S. González,et al.  The pitting and crevice corrosion of 304 stainless steel in phosphate-borate buffer containing sodium chloride , 1992 .

[4]  F. Bolzoni,et al.  Corrosion inhibitors in reinforced concrete structures Part 2 – Repair system , 2006 .

[5]  Z. Szklarska‐Śmiałowska,et al.  Pitting And Crevice Corrosion , 2004 .

[6]  M. R. Jones,et al.  Comparative performance of chloride attenuating and corrosion inhibiting systems for reinforced concrete , 2004 .

[7]  C. Andrade,et al.  Quantitative measurements of corrosion rate of reinforcing steels embedded in concrete using polarization resistance measurements , 1978 .

[8]  P. Marcus,et al.  Mechanisms of Pitting Corrosion , 2011 .

[9]  Brian E. Conway,et al.  Modern Aspects of Electrochemistry , 1974 .

[10]  M. Montemor,et al.  CHLORIDE-INDUCED CORROSION ON REINFORCING STEEL: FROM THE FUNDAMENTALS TO THE MONITORING TECHNIQUES , 2003 .

[11]  Daniel Cusson,et al.  Corrosion-Inhibiting Systems for Durable Concrete Bridges. I: Five-Year Field Performance Evaluation , 2008 .

[12]  Jm Gaidis,et al.  The inhibition of chloride-induced corrosion in reinforced concrete by calcium nitrite , 1987 .

[13]  J. Galland,et al.  Electrochemical impedance of pits. Influence of the pit morphology , 1997 .

[14]  M. C. Alonso,et al.  Corrosion inhibition of carbon steel in alkaline chloride media by Na3PO4 , 2007 .

[15]  C. L. Page,et al.  Corrosion inhibitors in concrete repair systems , 2000 .

[16]  Neal S. Berke,et al.  Predicting long-term durability of steel reinforced concrete with calcium nitrite corrosion inhibitor , 2004 .

[17]  M. Vazquez,et al.  The performance of a migrating corrosion inhibitor suitable for reinforced concrete , 2003 .

[18]  A. Sagüés,et al.  Technical Note: Crevice Effect on Corrosion of Steel in Simulated Concrete Pore Solutions , 2000 .

[19]  C. Monticelli,et al.  A study on corrosion inhibitors for concrete application , 2000 .

[20]  G. Fumagalli,et al.  A study of organic substances as inhibitors for chloride-induced corrosion in concrete , 2009 .

[21]  D. Mikulić,et al.  The inhibition activity of ascorbic acid towards corrosion of steel in alkaline media containing chloride ions , 2008 .

[22]  Bernhard Elsener,et al.  Corrosion inhibitors for steel in concrete: An EFC state of the art report , 2006 .

[23]  N. Sridhar,et al.  A general model for the repassivation potential as a function of multiple aqueous solution species , 2004 .

[24]  Han-seung Lee,et al.  Evaluation on the effect of lithium nitrite corrosion inhibitor by the corrosion sensors embedded in mortar , 2007 .

[25]  C. L. Page,et al.  Corrosion inhibitor systems for remedial treatment of reinforced concrete. Part 1: calcium nitrite , 2002 .

[26]  M. Nagumo,et al.  The effect of chloride concentration on early stages of pitting for type 304 stainless steel revealed by the AC impedance method , 1997 .

[27]  M. Valcarce,et al.  Carbon steel passivity examined in solutions with a low degree of carbonation: The effect of chloride and nitrite ions , 2009 .

[28]  Mark G. Richardson,et al.  Corrosion inhibitors for steel in concrete: State-of-the-art report , 2008 .

[29]  R. Balasubramaniam,et al.  On the corrosion behaviour of phosphoric irons in simulated concrete pore solution , 2008 .

[30]  C. Andrade,et al.  Effect of Carbonation, Chlorides and Relative Ambient Humidity on the Corrosion of Galvanized Rebars Embedded in Concrete , 1982 .

[31]  G. Frankel.  Pitting Corrosion of Metals A Review of the Critical Factors , 1998 .

[32]  A. Sagüés,et al.  Chloride Corrosion Threshold of Reinforcing Steel in Alkaline Solutions—Cyclic Polarization Behavior , 2002 .

[33]  J. Mankowski,et al.  Crevice corrosion of stainless steels in sodium chloride solution , 1979 .

[34]  J. R. Mackechnie,et al.  Performance of a Penetrating Corrosion Inhibitor in Concrete Affected by Carbonation-Induced Corrosion , 2006 .

[35]  C. Andrade,et al.  Electrochemical study of corrosion inhibition of steel reinforcement in alkaline solutions containing phosphates based components , 2007 .

[36]  Michel Keddam,et al.  Application of impedance technique to localized corrosion , 1988 .

[37]  M. Valcarce,et al.  Carbon steel passivity examined in alkaline solutions: The effect of chloride and nitrite ions , 2008 .

[38]  J. Galvele,et al.  Tafel’s law in pitting corrosion and crevice corrosion susceptibility , 2005 .

[39]  Vincent Vivier,et al.  Single pit on iron generated by SECM: An electrochemical impedance spectroscopy investigation , 2008 .

[40]  F. Mansfeld,et al.  Detection of Pitting with Electrochemical Impedance Spectroscopy , 1988 .

[41]  A. Sagüés,et al.  NITRITE DIFFUSIVITY IN CALCIUM NITRITE-ADMIXED HARDENED CONCRETE , 2003 .

[42]  C. Monticelli,et al.  Corrosion inhibition of steel in chloride-containing alkaline solutions , 2002 .

[43]  F. Mansfeld,et al.  Pitting and surface modification of SIC/Al , 1987 .

[44]  S. M. Sharland,et al.  A review of the theoretical modelling of crevice and pitting corrosion , 1987 .

[45]  Lorenzo Fedrizzi,et al.  THE USE OF MIGRATING CORROSION INHIBITORS TO REPAIR MOTORWAYS' CONCRETE STRUCTURES CONTAMINATED BY CHLORIDES , 2005 .

[46]  K. Sideris,et al.  Influence of calcium nitrite inhibitor on the durability of mortars under contaminated chloride and sulphate environments , 2004 .

[47]  C. M. Rangel,et al.  Use of EIS, ring-disk electrode, EQCM and Raman spectroscopy to study the film of oxides formed on iron in 1 M NaOH , 2002 .

[48]  Maria de Fátima Montemor,et al.  Corrosion behaviour of reinforcing steel exposed to an amino alcohol based corrosion inhibitor , 2005 .

[49]  M. Sluyters-Rehbach,et al.  The analysis of electrode impedances complicated by the presence of a constant phase element , 1984 .

[50]  Theodore W. Bremner,et al.  Influence of calcium nitrite inhibitor and crack width on corrosion of steel in high performance concrete subjected to a simulated marine environment , 2004 .

[51]  M. Montemor,et al.  Electrochemical behaviour of amino alcohol-based inhibitors used to control corrosion of reinforcing , 2004 .

[52]  Marta Castellote,et al.  Accelerated simultaneous determination of the chloride depassivation threshold and of the non-stationary diffusion coefficient values , 2002 .

[53]  P. Marcus,et al.  Corrosion Mechanisms in Theory and Practice , 1995 .

[54]  C. Andrade,et al.  Effect of nitrite in corrosion of reinforcing steel in neutral and acid solutions simulating the electrolytic environments of micropores of concrete in the propagation period , 2008 .

[55]  Josef Tritthart,et al.  Transport of a surface-applied corrosion inhibitor in cement paste and concrete , 2003 .

[56]  F. Hunkeler,et al.  PIT GROWTH MEASUREMENTS ON STAINLESS STEELS , 1983 .

[57]  Asuncion Bautista,et al.  The behaviour of pre-rusted steel in concrete , 1996 .