Fracture Mechanisms of Structural and Functional Multilayer Ceramic Structures

The fracture of mechanically loaded ceramics is a consequence of material critical defects located either within the bulk or at the surface, resulting from the processing and/or machining and handling procedures. The size and type of these defects determine the mechanical strength of the specimens, yielding a statistically variable strength and brittle fracture which limits their use for load-bearing applications. In recent years the attempt to design bio-inspired multilayer ceramics has been proposed as an alternative choice for the design of structural components with improved fracture toughness (e.g. through energy release mechanisms such as crack branching or crack deflection) and mechanical reliability (i.e. flaw tolerant materials). This approach could be extended to complex multilayer engineering components such as piezoelectric actuators or LTCCs (consisting of an interdigitated layered structure of ceramic layers and thin metal electrodes) in order to enhance their performance functionality as well as ensuring mechanical reliability. In this work the fracture mechanisms in several structural and functional multilayer components are investigated in order to understand the role of the microstructure and layered architecture (e.g. metal-ceramic or ceramic-ceramic) on their mechanical behaviour. Design guidelines based on experiments and theoretical approaches are given aiming to enhance the reliability of multilayer components.

[1]  A. A. Griffith.  The Phenomena of Rupture and Flow in Solids , 1921 .

[2]  W. D. Kingery,et al.  Introduction to Ceramics , 1976 .

[3]  A. Evans.  Perspective on the Development of High‐Toughness Ceramics , 1990 .

[4]  K. Kendall,et al.  A simple way to make tough ceramics , 1990, Nature.

[5]  Robert Danzer,et al.  A general strength distribution function for brittle materials , 1992 .

[6]  Kenji Uchino,et al.  Piezoelectric Actuators and Ultrasonic Motors , 1996 .

[7]  C. Lynch.  Fracture of ferroelectric and relaxor electro-ceramics: influence of electric field 1 1 Work begun d , 1998 .

[8]  Rao,et al.  Laminar Ceramics That Exhibit a Threshold Strength. , 1999, Science.

[9]  J. J. Mecholsky.  Fractography of Brittle Materials , 2001 .

[10]  N. Setter,et al.  Piezoelectric materials in devices , 2002 .

[11]  Ulrich Schmid,et al.  Lifetime prediction for mechanically stressed low temperature co-fired ceramics , 2004 .

[12]  Yoshihiko Imanaka,et al.  Multilayered low temperature cofired ceramics (LTCC) technology , 2004 .

[13]  R. Bermejo,et al.  Thermal Shock Behavior of an Al2O3/ZrO2 Multilayered Ceramic with Residual Stresses due to Phase Transformations , 2005 .

[14]  D. Munz,et al.  Nonsymmetric Deformation Behavior of Lead Zirconate Titanate Determined in Bending Tests , 2005 .

[15]  Eduardo Saiz,et al.  Freezing as a Path to Build Complex Composites , 2006, Science.

[16]  R. Danzer,et al.  The ball on three balls test—Strength and failure analysis of different materials , 2007 .

[17]  A. Sanchez-Herencia,et al.  High-temperature mechanical behaviour of flaw tolerant alumina–zirconia multilayered ceramics , 2007 .

[18]  Robert Danzer,et al.  Fracture of Ceramics , 2008 .

[19]  R. Bermejo,et al.  Fatigue Behavior of Alumina–Zirconia Multilayered Ceramics , 2008 .

[20]  R. Ritchie,et al.  Tough, Bio-Inspired Hybrid Materials , 2008, Science.

[21]  L. Ceseracciu,et al.  Fracture of Layered Ceramics , 2009 .

[22]  R. Ritchie,et al.  On the Fracture Toughness of Advanced Materials , 2009 .

[23]  R. Bermejo,et al.  Influence of Internal Architectures on the Fracture Response of LTCC Components , 2009 .

[24]  R. Bermejo,et al.  High failure resistance layered ceramics using crack bifurcation and interface delamination as reinforcement mechanisms , 2010 .