The flame retardant mechanism of polyolefins modified with chalk and silicone elastomer

This paper presents the current understanding of the flame retardant mechanism of Casico™. The study includes the flame retardant effect of each individual component: ethylene–acrylate copolymer, chalk and silicone elastomer, as well as the formation of an intumescent structure during heating. The flame retardant properties were investigated by cone calorimetry and oxygen index tests. To obtain insight into the flame retardant mechanism, heat treatment under different conditions has also been performed. The results indicate that the flame retardant mechanism of Casico is complex and is related to a number of reactions, e.g. ester pyrolysis of acrylate groups, formation of carbon dioxide by reaction between carboxylic acid and chalk, ionomer formation and formation of an intumescent structure stabilized by a protecting char. Special emphasis is given to the formation of the intumescent structure and its molecular structure as evaluated from 13C MAS-NMR and 29Si MAS-NMR, ESCA and XRD analysis. After treatment at 500°C the intumescent structure consists mainly of silicon oxides and calcium carbonate and after treatment at 1000°C the intumescent structure consists of calcium silicate, calcium oxide and calcium hydroxide. Copyright © 2003 John Wiley & Sons, Ltd.

[1]  E. Sörvik,et al.  Thermal degradation of polyethylene in a nitrogen atmosphere of low oxygen content , 1970 .

[2]  G. Maciel,et al.  Silicon-29 NMR study of the surface of silica gel by cross polarization and magic-angle spinning , 1980 .

[3]  Gordon L. Nelson,et al.  Fire and Polymers: An Overview , 1995 .

[4]  Bernt-Åke Sultan,et al.  Thermal degradation of EVA and EBA—A comparison. II. Changes in unsaturation and side group structure , 1991 .

[5]  A. Brandolini,et al.  NMR Spectra of Polymers and Polymer Additives , 2000 .

[6]  A. Brough,et al.  Si NMR Study of the Hydration of Ca3SiO5 and ß‐Ca2SiO4 in the Presence of Silica Fume , 2004 .

[7]  M. Hunter,et al.  Organo-silicon polymers; the cyclic dimethyl siloxanes. , 1946, Journal of the American Chemical Society.

[8]  C. W. Lewis.  The pyrolysis of dimethylpolysitloxanes. II , 1959 .

[9]  N. Grassie,et al.  The thermal degradation of polysiloxanes—I. Poly(dimethylsiloxane) , 1978 .

[10]  T. Thomas,et al.  Thermal analysis of polydimethylsiloxanes. I. Thermal degradation in controlled atmospheres , 1969 .

[11]  Gasification of silicone fluids under external thermal radiation. Part I. Gasification rate and global heat of gasification , 1998 .

[12]  G. Maciel,et al.  Silicon-29 NMR study of dehydrated/rehydrated silica gel using cross polarization and magic-angle spinning , 1983 .

[13]  M. Kučera,et al.  Neutralization of residual catalyst in polydimethylsiloxane. effect of neutralization on the thermal stability of the polymer , 1961 .

[14]  Bernt-Åke Sultan,et al.  Thermal degradation of EVA and EBA—A comparison. I. Volatile decomposition products , 1991 .

[15]  Gerald Scott,et al.  Polymer Degradation and Stabilisation , 1988 .

[16]  W. C. Kuryla,et al.  Flame retardancy of polymeric materials , 1973 .