Fracture mechanical characterization of fibre reinforced plastics in the intralaminar crack opening mode (mode I) and in the shear mode (mode II)

[1]  E. Tschegg,et al.  Radiation effects on insulators for superconducting fusion magnets , 1995 .

[2]  E. Tschegg,et al.  Fracture tests in Mode I on fibre-reinforced plastics , 1993 .

[3]  E. Tschegg,et al.  Influence of test geometry on tensile strength of fibre reinforced plastics at cryogenic temperatures , 1991 .

[4]  S. Nishijima,et al.  Radiation damage of organic composite material for fusion magnet , 1991 .

[5]  S. Egusa.  Anisotropy of radiation-induced degradation in mechanical properties of fabric-reinforced polymer-matrix composites , 1990 .

[6]  Anthony J. Kinloch,et al.  The analysis of interlaminar fracture in uniaxial fibre-polymer composites , 1990, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[7]  J. Davies.  Numerical study of punch-through shear specimen in mode II testing for cementitious materials , 1988 .

[8]  Jan Backlund,et al.  Tensile Fracture of Laminates with Cracks , 1986 .

[9]  Shaw Ming Lee,et al.  A Comparison of Fracture Toughness of Matrix Controlled Failure Modes: Delamination and Transverse Cracking: , 1986 .

[10]  A. Hillerborg.  The theoretical basis of a method to determine the fracture energyGF of concrete , 1985 .

[11]  Z. Bažant.  Size Effect in Blunt Fracture: Concrete, Rock, Metal , 1984 .

[12]  H. Hilsdorf,et al.  Fracture mechanics studies on concrete compounds , 1977 .

[13]  E. K. Tschegg,et al.  Mode II fracture tests on fibre-reinforced plastics , 1995, Journal of Materials Science.

[14]  E. Tschegg,et al.  Small specimens and new testing techniques for fiber reinforced plastics in the crack opening mode (mode I) and in the shear mode (mode II) , 1994 .

[15]  E. Tschegg,et al.  Specimen size effect on tensile strength of three-dimensionally glass-fabric reinforced plastics at room and cryogenic temperatures , 1993 .

[16]  E. Tschegg,et al.  Fracture-Mechanical Characterization of Fiber Reinforced Plastics in the Crack-Opening-Mode (Mode I) , 1992 .

[17]  E. Tschegg,et al.  Shear Fracture Tests (Mode II) on Fiber Reinforced Plastics at Room and Cryogenic Temperatures , 1992 .

[18]  S. K. Maiti,et al.  Prediction of mode I fracture toughness of a laminated fibre composite from matrix fracture toughness of the basic layer , 1991 .

[19]  J. Williams,et al.  Mechanics and mechanisms of delamination in a poly(ether sulphone)—Fibre composite , 1990 .

[20]  J. Ahmad,et al.  A simple technique for measuring mode I delamination energy release rate in polymeric composites , 1989 .

[21]  G. S. Giare,et al.  Fracture toughness of unidirectional graphite fibre reinforced/epoxy composite in mode ii (forward shear), using a thin tubular specimen , 1988 .

[22]  J. A. Barnes,et al.  Theoretical and experimental evaluation of the Iosipescu shear test , 1987 .

[23]  Carl-Gustaf Aronsson,et al.  Damage Mechanics Analysis of Matrix Effects in Notched Laminates , 1986 .

[24]  Amar C. Garg,et al.  Intralaminar and interlaminar fracture in graphite/epoxy laminates , 1986 .

[25]  O. Ishai,et al.  Hygrothermal Influence on Delamination Behavior of Graphite/Epoxy Laminates, , 1985 .