Degumming of silk fabric with several proteases.

A crêpe silk fabric was treated with different alkaline (3374-L, GC 897-H), neutral (3273-C), and acid (EC 3.4 23.18) proteases with the aim to study their effectiveness as degumming agents. Proteases were used under optimum conditions of pH and temperature, while enzyme dosage (0.05-2 U/g fabric) and treatment time (5-240 min) were changed in order to study the kinetics of sericin removal. Degumming loss with soap and alkali was 27 wt.%. The maximum amount of sericin removed in 1 h was 17.6, 24, and 19 wt.% for 3374-L (2 U/g fabric), GC 897-H (1U/g fabric), and 3273-C (0.1 U/g fabric), respectively. Under the experimental conditions adopted, EC 3.4 23.18 was almost ineffective as a degumming agent. Degumming loss increased as a function of the treatment time, reaching a value of 25 wt.% with 1 U/g fabric of 3374-L. The morphological analysis showed that sericin was completely removed from the warp yarns of the crêpe fabric, while the highly twisted weft yarns still exhibited the presence of sericin deposits within the most internal parts of the close fibre texture. The chromatographic pattern of soluble sericin peptides changed as a function of the kind of enzyme used, enzyme dosage, and treatment time. A mixture of peptides from 5 to 20 kDa in weight, with a weight-average molecular weight of about 12 kDa was obtained.

[1]  M. Gehoh,et al.  Crystal structure of silk (bombyx mori) , 1991 .

[2]  B. Lotz,et al.  The chemical structure and the crystalline structures of Bombyx mori silk fibroin. , 1979, Biochimie.

[3]  M. Gulrajani,et al.  Degumming of silk with lipase and protease , 2000 .

[4]  P. Radhakrishnaiah,et al.  Mechanical Agitation of Cotton Fabrics During Enzyme Treatment and Its Effect on Tactile Properties , 1999 .

[5]  R. Chattopadhyay,et al.  Low Stress Mechanical Properties of Silk Fabric Degummed by Different Methods , 1996 .

[6]  G M Gübitz,et al.  Biotechnology in the textile industry--perspectives for the new millennium. , 2001, Journal of biotechnology.

[7]  M. Rousselle,et al.  Enzymatic Treatment of Lyocell—Clarification of Depilling Mechanisms , 2000 .

[8]  M. Jacquet,et al.  Fine organization of Bombyx mori fibroin heavy chain gene. , 2000, Nucleic acids research.

[9]  Hans Laufer,et al.  Polypeptides of fibroin and sericin secreted from the different sections of the silk gland in Bombyx mori , 1977 .

[10]  P. Couble,et al.  Developmental switches of sericin mRNA splicing in individual cells of Bombyx mori silkgland. , 1987, Developmental biology.

[11]  G. Freddi,et al.  Use of HP-size exclusion chromatography to study the degree of polymerization of silk (Bombyx mori) fibroin fibres , 2000 .

[12]  M. Gulrajani,et al.  Degumming of silk with different protease enzymes , 1996 .

[13]  G. Deléage,et al.  Structure and organization of the Bombyx mori sericin 1 gene and of the sericins 1 deduced from the sequence of the Ser 1B cDNA. , 1997, Insect biochemistry and molecular biology.

[14]  Luis Almeida,et al.  Effects of Agitation and Endoglucanase Pretreatment on the Hydrolysis of Cotton Fabrics by a Total Cellulase , 1996 .