An alternate explanation for the abrupt current increase at the pitting potential

Abstract A critical transition potential is shown to be associated with the abrupt increase in the number of metastable pits and the onset of spatial clustering of pits amongst nearest neighbor defects in both commercial and model stainless steels. This critical transition potential is correlated with the parameter, E pit commonly observed in near-neutral NaCl solutions when stainless steels form pits. The explosive growth of pit sites, the onset of clustering of pits, and E pit all depend on the diffusion length associated with aggressive corrosion products formed at pits and thus on the stirring rate. E pit is observed to increase significantly and pit sites remain random to high potentials in both experiments and modeling when the diffusion length is decreased below the nearest neighbor distance (NND) associated with surface defects such as non-metallic inclusions that form a random array of susceptible sites across the otherwise passive surface. This phenomenon is confirmed by experiments and modeling using model stainless steel alloys with decreased inclusions densities and, thus, increased defect NNDs. If the NND is greater than the lateral diffusion length, then E pit will increase, clustering of pit sites will decrease and explosive growth in the number of pits will be suppressed at a given applied point.

[1]  J. Scully The corrosion of materials , 1989 .

[2]  E. Gileadi,et al.  Electrode Kinetics for Chemists, Chemical Engineers and Materials Scientists , 1993 .

[3]  David E. Williams,et al.  The initiation of pitting corrosion on austenitic stainless steel : on the role and importance of sulphide inclusions , 1992 .

[4]  Petrus Christiaan Pistorius,et al.  Metastable pitting corrosion of stainless steel and the transition to stability , 1992, Philosophical Transactions of the Royal Society of London. Series A: Physical and Engineering Sciences.

[5]  G. Frankel Pitting Corrosion of Metals A Review of the Critical Factors , 1998 .

[6]  William H. Smyrl,et al.  Scanning Electrochemical Microscopy of Precursor Sites for Pitting Corrosion on Titanium , 1993 .

[7]  H. White,et al.  Scanning Electrochemical Microscopy of Electroactive Defect Sites in the Native Oxide Film on Aluminum , 2001 .

[8]  David E. Williams,et al.  The nucleation, growth and stability of micropits in stainless steel , 1994 .

[9]  R. Wei,et al.  Microconstituent-Induced Pitting Corrosion in Aluminum Alloy 2024-T3 , 1996 .

[10]  Wei Gao,et al.  Effects of nitric acid passivation on the pitting resistance of 316 stainless steel , 2000 .

[11]  C. P. Dillon Cleaning, pickling, and passivation of stainless steels , 1994 .

[12]  P. Marcus,et al.  The influence of sulphur on the dissolution and the passivation of a nickel-iron alloy—I. electrochemical and radiotracer measurements , 1984 .

[13]  B. Baroux,et al.  The kinetics of pit generation on stainless steels , 1988 .

[14]  T. A. Hatton,et al.  Mass transfer and electrochemical kinetic interactions in localized pitting corrosion , 1986 .

[15]  John L. Hudson,et al.  Interactions among metastable pits on heterogeneous electrodes , 2007 .

[16]  A S Mikhailov,et al.  Sudden Onset of Pitting Corrosion on Stainless Steel as a Critical Phenomenon , 2004, Science.

[17]  R. H. Titran Niobium and its alloys , 1992 .

[18]  M. Ryan,et al.  Corrosion Pits in Thin Films of Stainless Steel , 1999 .

[19]  Zhe Jiang,et al.  Spatial Statistics , 2013 .

[20]  J. Nývlt Nucleation , 1991 .

[21]  G. Glass,et al.  The presentation of the chloride threshold level for corrosion of steel in concrete , 1997 .

[22]  J. L. Hudson,et al.  Spatial Interactions among Localized Corrosion Sites Experiments and Modeling , 2002 .

[23]  R. Alkire,et al.  Local Detection of Dissolved Sulfur Species from Inclusions in Stainless Steel Using Ag Microelectrode , 2001 .

[24]  R. Newman,et al.  Perforated Covers for Propagating Pits , 1998 .

[25]  David E. Williams,et al.  Studies of the initiation of pitting corrosion on stainless steels , 1984 .

[26]  H. Holtan,et al.  Determination of characteristic pitting potentials for aluminium by use of the potentiostatic methods , 1977 .

[27]  J. L. Hudson,et al.  A spatiotemporal model of interactions among metastable pits and the transition to pitting corrosion , 2005 .

[28]  W. Smyrl,et al.  Pitting Corrosion of Titanium , 1994 .

[29]  John L. Hudson,et al.  Cooperative Stochastic Behavior in Localized Corrosion I. Model , 1997 .

[30]  R. Newman,et al.  The mechanism of lacy cover formation in pitting , 1997 .

[31]  J. L. Hudson,et al.  Origins of Persistent Interactions Among Localized Corrosion Sites , 2002 .

[32]  Cooperative Spreading of Pit Sites as a New Explanation for Critical Threshold Potentials , 2006 .

[33]  H. White,et al.  Chemically-selective and spatially-localized redox activity at Ta/Ta2O5 electrodes , 1999 .

[34]  David E. Williams,et al.  Elucidation of a Trigger Mechanism for Pitting Corrosion of Stainless Steels Using Submicron Resolution Scanning Electrochemical and Photoelectrochemical Microscopy , 1998 .

[35]  R. Kelly,et al.  In Situ Confocal Laser Scanning Microscopy of AA 2024-T3 Corrosion Metrology I. Localized Corrosion of Particles , 2004 .

[36]  Richard C. Alkire,et al.  Pit Initiation at Single Sulfide Inclusions in Stainless Steel I. Electrochemical Microcell Measurements , 2002 .

[37]  R. Brigham,et al.  Temperature as a Pitting Criterion , 1973 .

[38]  Omar Suliman Zaroog,et al.  Corrosion of Stainless Steels , 1979 .

[39]  Z. Szklarska‐Śmiałowska,et al.  Pitting Corrosion of Metals , 1986 .

[40]  F. Mansfeld,et al.  Technical Note: The Effect of Rotation on Pitting Behavior of Aluminum and Stainless Steel , 1979 .

[41]  J. L. Hudson,et al.  Detection of Interactions among Localized Pitting Sites on Stainless Steel Using Spatial Statistics , 2005 .