Convergent Pad Polishing of Amorphous Silica

A new method of optical polishing termed “Convergent Polishing” is demonstrated where a workpiece, regardless of its initial surface figure, will converge to the lap shape in a single iteration. This method of polishing is accomplished by identifying the phenomena that contribute to non-uniform spatial material removal, and mitigating the non-uniformity for each phenomenon (except for the workpiece-lap mismatch due to the workpiece surface shape). The surface mismatch at the interface between the workpiece and lap causes a spatial and time varying pressure differential which decreases with removal, thus allowing the workpiece to converge to the shape of the lap. In this study, fused (amorphous) silica workpieces are polished using ceria slurry on various polyurethane pads. Polishing parameters were systematically controlled to prevent various sources of non-uniform material removal which include: (i) moment force, (ii) viscoelastic lap relaxation, (iii) kinematics, (iv) pad wear, and (v) workpiece bending. The last two are described herein. With these mitigations, removal uniformity has been demonstrated to within 1.0 μm over the surface after 83 μm of material removal corresponding to a within workpiece non-uniformity (WIWNU) of <1.2%. Also, convergence has been demonstrated down to 0.18 ± 0.04 μm peak-to-valley flatness on 100 mm-sized workpieces.

[1]  S. Danyluk,et al.  Wafer-Bending Measurements in CMP , 2004 .

[2]  Hong Liang,et al.  Tribology In Chemical-Mechanical Planarization , 2005 .

[3]  L. Cook.  Chemical processes in glass polishing , 1990 .

[4]  F W Preston,et al.  The structure of abraded glass surfaces , 1922 .

[5]  Marius K. Orlowski,et al.  A statistical polishing pad model for chemical-mechanical polishing , 1993, Proceedings of IEEE International Electron Devices Meeting.

[6]  Yuzhuo Li,et al.  Microelectronic Applications of Chemical Mechanical Planarization , 2007 .

[7]  Sang-Shin Park,et al.  Hydrodynamic analysis of chemical mechanical polishing process , 2000 .

[8]  Robert D. Tolles,et al.  Chemical Mechanical Polishing of Interlevel Dielectrics: Models for Removal Rate and Planarity , 1992 .

[9]  Y. Jeng,et al.  Impact of Abrasive Particles on the Material Removal Rate in CMP A Microcontact Perspective , 2004 .

[10]  D. Golini,et al.  Twyman effect mechanics in grinding and microgrinding. , 1996, Applied optics.

[11]  A J Dalladay,et al.  Some measurements of the stresses produced at the surfaces of glass by grinding with loose abrasives , 1922 .

[12]  C. Fred Higgs,et al.  Hydrodynamics of Slurry Flow in Chemical Mechanical Polishing A Review , 2006 .

[13]  David Dornfeld,et al.  Material removal mechanism in chemical mechanical polishing: theory and modeling , 2001 .

[14]  H. Saunders,et al.  Formulas for Stress and Strain – 5th Edition , 1979 .

[15]  H. W. LEE,et al.  Prism and Lens Making , 1943, Nature.

[16]  Yeau-Ren Jeng,et al.  Tribological Analysis of CMP with Partial Asperity Contact , 2003 .

[17]  T. Suratwala,et al.  Material removal and surface figure during pad polishing of fused silica , 2009 .

[18]  O. Podzimek,et al.  Residual Stress and Deformation Energy Under Ground Surfaces of Brittle Solids , 1986 .

[19]  T. Suratwala,et al.  The effect of HF/NH4F etching on the morphology of surface fractures on fused silica , 2008 .

[20]  S. R. Runnels,et al.  Tribology Analysis of Chemical‐Mechanical Polishing , 1994 .

[21]  P. Miller,et al.  Sub-surface mechanical damage distributions during grinding of fused silica , 2005 .

[22]  Ki-Hyun Park,et al.  Pad roughness variation and its effect on material removal profile in ceria-based CMP slurry , 2008 .

[23]  Ingrid De Wolf,et al.  Study of damage and stress induced by backgrinding in Si wafers , 2003 .

[24]  Michael D. Feit,et al.  Toward Deterministic Material Removal and Surface Figure During Fused Silica Pad Polishing , 2010 .

[25]  T. Cale,et al.  Von Mises Stress in Chemical‐Mechanical Polishing Processes , 1997 .

[26]  Ki-Hyun Park,et al.  Mathematical modeling of CMP conditioning process , 2007 .

[27]  Variation of polish pad shape during pad dressing , 1999 .

[28]  Cheng-Ching Yu,et al.  Operational Aspects of Chemical Mechanical Polishing Polish Pad Profile Optimization , 2000 .