A new method for fabricating zirconia copings using a Nd:YVO4 nanosecond laser.

The purpose of this work was to fabricate zirconia copings from fully sintered Y-TZP blocks using a Nd:YVO4 nanosecond laser in order to avoid complicated procedures using conventional CAD/CAM systems. To determine the most appropriate power level of a Nd:YVO4 laser, cuboid fully sintered Y-TZP specimens were irradiated at six different average power levels. One-way ANOVAs for the average surface roughness and laser machining depth revealed that an average power level of 7.5 W generated a smooth machined surface with high machining efficiency. Y-TZP copings were then machined using the proposed method with the most appropriate power level. As the number of machining iterations increased, the convergence angles decreased significantly (p<0.01). The accuracy of the machined copings was judged to be good based on 3D measurements and traditional metal die methods. The proposed method using the nanosecond laser was demonstrated to be useful for fabricating copings from fully sintered Y-TZP.

[1]  R. Conroy,et al.  Q-switching of a diode-pumped Nd:YVO4 laser using a quadrupole electro-optic deflector , 1998 .

[2]  S. Ban,et al.  Surface damages of zirconia by Nd:YAG dental laser irradiation. , 2010, Dental materials journal.

[3]  G. Sjögren,et al.  Clinical examination of leucite-reinforced glass-ceramic crowns (Empress) in general practice: a retrospective study. , 1999, The International journal of prosthodontics.

[4]  Daniel Edelhoff,et al.  Marginal and internal fits of fixed dental prostheses zirconia retainers. , 2009, Dental materials : official publication of the Academy of Dental Materials.

[5]  Yoshihiro Tanaka,et al.  Blackening and crack formation in Q-switched YAG laser machining of zirconia ceramics. , 1989 .

[6]  T. Yamagishi,et al.  Mechanical properties of laser welds of titanium in dentistry by pulsed Nd:YAG laser apparatus. , 1993, The Journal of prosthetic dentistry.

[7]  Igor J Pesun,et al.  Current ceramic materials and systems with clinical recommendations: a systematic review. , 2007, The Journal of prosthetic dentistry.

[8]  Martin F. Land Dds Msd,et al.  Contemporary Fixed Prosthodontics , 2001 .

[9]  J. G. Crowder,et al.  Development of Optical Techniques for Noncontact Inspection of Y–TZP Parts , 2011 .

[10]  J. Mclean,et al.  The estimation of cement film thickness by an in vivo technique , 1971, British Dental Journal.

[11]  Duncan P. Hand,et al.  Optimized Nanosecond Pulsed Laser Micromachining of Y‐TZP Ceramics , 2008 .

[12]  Kaan Erkorkmaz,et al.  Time-optimal trajectory generation for 5-axis on-the-fly laser drilling , 2011 .

[13]  Carsten Korte,et al.  Electrochemical blackening of yttria-stabilized zirconia – morphological instability of the moving reaction front , 1999 .

[14]  S. Koutayas,et al.  Zirconia in dentistry: Part 1. Discovering the nature of an upcoming bioceramic. , 2009, The European journal of esthetic dentistry : official journal of the European Academy of Esthetic Dentistry.

[15]  Julie A. Holloway,et al.  Ceramics for Dental Applications: A Review , 2010, Materials.

[16]  Giuseppe Casalino,et al.  An artificial neural network approach for the control of the laser milling process , 2012, The International Journal of Advanced Manufacturing Technology.