Highly efficient infrared-to-visible energy upconversion in Er(3+):Y(2)O(3).

Very intense green and red emission was observed at room temperature from the (4)S(3/2) and (4)F(9/2) levels of Er(3+):Y(2)O(3). A cw diode laser at 975 nm was used as a pump for resonant sequential excitation of the (4)I(11/2) and (4)F(7/2) levels. The fluorescence was easily visible to the naked eye, even with 27 mW of excitation power. It was found that at 850 mW of cw excitation power the total luminance was 39,000 cd/m(2). This corresponds to ~100 muW of green emission and 270 muW of red emission.

[1] Younes Messaddeq,et al. Optical spectroscopy of Er3+ and Yb3+ co-doped fluoroindate glasses , 1998 .

[2] Y. Messaddeq,et al. Infrared‐to‐visible CW frequency upconversion in Er3+‐doped fluoroindate glasses , 1996 .

[3] Younes Messaddeq,et al. Frequency upconversion in Er3+-doped fluoroindate glasses pumped at 1.48 μm , 1997 .

[4] K. Soga,et al. UPCONVERSION MECHANISM IN ER3+-DOPED FLUOROZIRCONATE GLASSES UNDER 800 NM EXCITATION , 1999 .

[5] Putcha Venkateswarlu,et al. Infrared to visible energy upconversion in Er3+‐doped oxide glass , 1994 .

[6] R. Macfarlane,et al. Green infrared‐pumped erbium upconversion laser , 1987 .

[7] W. Denk,et al. Two-photon laser scanning fluorescence microscopy. , 1990, Science.

[8] Xiaopeng Wang,et al. A chemically labeled cytotoxic agent: two-photon fluorophore for optical tracking of cellular pathway in chemotherapy. , 1999, Proceedings of the National Academy of Sciences of the United States of America.

[9] Markus Pollnau,et al. Near-infrared to visible upconversion in Er 3+ doped Cs 3 Lu 2 Cl 9 , Cs 3 Lu 2 Br 9 , and Cs 3 Y 2 I 9 excited at 1.54 µm , 1999 .