Self-lubricating behaviors of Al2O3/TiB2 ceramic tools in dry high-speed machining of hardened steel

Abstract In this paper, Al 2 O 3 /TiB 2 ceramic cutting tools with different TiB 2 content were produced by hot pressing. The fundamental properties of these ceramic cutting tools were examined. Dry high-speed machining tests were carried out on hardened steel. The tool wear, the cutting temperature, the cutting forces, and the friction coefficient between the tool and the chip were measured. It was shown that both the wear rates and the friction coefficient at the tool–chip interface of Al 2 O 3 /TiB 2 ceramic cutting tools in dry high-speed machining of hardened steel were reduced compared with that of in low-speed machining. The mechanisms responsible were determined to be the formation of a self-lubricating oxide film on the tool–chip interface owing to the tribological–chemical reaction by the elevated cutting temperature. The composition of the self-lubricating film was found to be the oxidation product of TiB 2 grains, which serves as lubricating additive on the wear track of the tool rake face. The appearance of this self-lubricating oxide film contributed to the improvement in wear resistance and the decrease of the friction coefficient. This action was even more effective with higher TiB 2 content. Cutting speed was found to have a profound effect on the self-lubricating behavior. In dry low-speed machining of hardened steel, the Al 2 O 3 /TiB 2 tools showed mainly adhesive and abrasive wear. While in dry high-speed machining, oxidation wear of the ceramic tools was the dominant mechanism due to the very high cutting temperature. No oxide film was formed on the tool–chip interface while machining in nitrogen atmosphere, and the tool wear resistance was correspondingly decreased.

[1]  Harold E. Sliney,et al.  Solid lubricant materials for high temperatures: A review , 1982 .

[2]  M. Fine,et al.  Tribological Behavior of SiC‐Whisker/Al2O3 Composites against Carburized 8620 Steel in Lubricated Sliding , 1991 .

[3]  J. Matsushita,et al.  Oxidation of TiB2-Al2O3 Composites in Air , 1990 .

[4]  E. Ezugwu,et al.  An overview of the machinability of aeroengine alloys , 2003 .

[5]  Janez Kopac,et al.  Wear mechanisms of cutting tools in high-speed cutting processes , 2001 .

[6]  G. Brandt,et al.  Ceramic Cutting Tools, State of the Art and Development Trends , 1999 .

[7]  G. Brandt,et al.  Wear mechanisms of ceramic cutting tools when machining ferrous and non-ferrous alloys , 1990 .

[8]  R. Steinbrech.  Toughening mechanisms for ceramic materials , 1992 .

[9]  Herbert Schulz,et al.  High-Speed Machining , 1992 .

[10]  Matz Lenner,et al.  High Speed Machining , 2001 .

[11]  Yasuo Yamane,et al.  A New Advanced Ceramic for Dry Machining , 1997 .

[12]  A. Xing,et al.  Wear behavior and mechanisms of alumina-based ceramic tools in machining of ferrous and non-ferrous alloys , 1997 .

[13]  R. Cook,et al.  A Modified Indentation Toughness Technique , 1983 .

[14]  A. Xing,et al.  Friction and wear behavior of Al2O3/TiB2 composite against cemented carbide in various atmospheres at elevated temperature , 1996 .

[15]  F. Klocke,et al.  Testing and Design of Tool Coatings with Properties Adapted to the Use of Biodegradable Cutting Fluids , 2001 .

[16]  P. Sreejith,et al.  Dry machining: Machining of the future , 2000 .

[17]  Ranga Komanduri,et al.  Nanocoatings on Cutting Tools For Dry Machining , 1997 .

[18]  E. D. Whitney,et al.  Microstructural engineering of ceramic cutting tools , 1988 .

[19]  Jianxin Deng.  WEAR, LUBRICATION AND MATCHING OF CERAMIC CUTTING TOOLS WITH THE WORKPIECE MATERIALS , 2002 .

[20]  Mahmudur Rahman,et al.  Experimental Evaluation on the Effect of Minimal Quantities of Lubricant in Milling , 2002 .

[21]  J. Hodowany,et al.  MODELING THE PHYSICS OF METAL CUTTING IN HIGH-SPEED MACHINING , 1998 .

[22]  A. Evans.  Perspective on the Development of High‐Toughness Ceramics , 1990 .

[23]  Fritz Klocke,et al.  Coated Tools for Metal Cutting – Features and Applications , 1999 .

[24]  Anselmo Eduardo Diniz,et al.  Using a minimum quantity of lubricant (MQL) and a diamond coated tool in the drilling of aluminum–silicon alloys , 2002 .

[25]  D. Aspinwall,et al.  A review of ultra high speed milling of hardened steels , 1997 .