Investigating the effect of metal oxide additives on the properties of Cu/ZnO/Al2O3 catalysts in methanol synthesis from syngas using factorial experimental design

The Cu/ZnO/Al2O3 catalysts, prepared by co-precipitation method, have been modified by adding small amount of Mn, Mg, Zr, Cr, Ba, W and Ce oxides using design of experiments (1/16 full factorial design). The structure and morphology of catalysts were studied by X-ray diffraction (XRD) and BET. Performance of the prepared catalysts for CO/CO2 hydrogenation to methanol was evaluated by using a stainless steel fixed-bed reactor at 5 MPa and 513 K. The oxide additives were found to influence the catalytic activity, dispersion of Cu, Cu crystallite size, surface composition of catalyst and stability of catalysts during their operations. The results showed that the Mn and Zr promoted catalysts have high performance for methanol synthesis from syngas.

[1]  Y. Suh,et al.  Active sites in Cu/ZnO/ZrO2 catalysts for methanol synthesis from CO/H2 , 2000 .

[2]  M. Saito,et al.  Activity and stability of Cu/ZnO/Al2O3 catalyst promoted with B2O3 for methanol synthesis , 2000 .

[3]  M. Wainwright,et al.  The influence of Cr, Zn and Co additives on the performance of skeletal copper catalysts for methanol synthesis and related reactions , 2004 .

[4]  J. Fierro,et al.  Pd-Modified Cu-Zn Catalysts for Methanol Synthesis from CO2/H2 Mixtures: Catalytic Structures and Performance , 2002 .

[5]  Pilar Ramírez de la Piscina,et al.  Highly effective conversion of CO2 to methanol over supported and promoted copper-based catalysts: influence of support and promoter , 2001 .

[6]  J. W. Evans,et al.  On the determination of copper surface area by reaction with nitrous oxide , 1983 .

[7]  Mustafa Soylak,et al.  Optimization of microwave assisted digestion procedure for the determination of zinc, copper and nickel in tea samples employing flame atomic absorption spectrometry. , 2007, Journal of hazardous materials.

[8]  A. Kozłowska,et al.  Effect of Mg and Mn oxide additions on structural and adsorptive properties of Cu/ZnO/ZrO2 catalysts for the methanol synthesis from CO2 , 2003 .

[9]  J. Fierro,et al.  CO2 hydrogenation over Pd-modified methanol synthesis catalysts , 1998 .

[10]  Piotr Olszewski,et al.  Effect of metal oxide additives on the activity and stability of Cu/ZnO/ZrO2 catalysts in the synthesis of methanol from CO2 and H2 , 2006 .

[11]  H. Y. Chen,et al.  Comparative studies of manganese-doped copper-based catalysts: the promoter effect of Mn on methanol synthesis , 1998 .

[12]  Yoshinori Kanamori,et al.  Preparation of a coprecipitated Cu/ZnO catalyst for the methanol synthesis from CO2 — effects of the calcination and reduction conditions on the catalytic performance , 2001 .

[13]  HuaWang,et al.  Influence of Aging Time on the Properties of Precursors of CuO／ZnO Catalysts for Methanol Synthesis , 2005 .

[14]  K. Jun,et al.  Residual sodium effect on the catalytic activity of Cu/ZnO/Al2O3 in methanol synthesis from CO2 hydrogenation , 1998 .

[15]  Masami Takeuchi,et al.  The stability of Cu/ZnO-based catalysts in methanol synthesis from a CO2-rich feed and from a CO-rich feed , 2001 .

[16]  Jian Li,et al.  Characterization of precursors of methanol synthesis catalysts, copper/zinc/aluminum oxides, precipitated at different pHs and temperatures , 1996 .

[17]  Chi-Chang Hu,et al.  Pore-size dependence of AAO films on surface roughness of Al-1050 sheets controlled by electropolishing coupled with fractional factorial design , 2007 .

[18]  S. Fujita,et al.  Methanol synthesis from CO2 over Cu/ZnO catalysts prepared from various coprecipitated precursors , 1998 .

[19]  T. Johannessen,et al.  An improved N2O-method for measuring Cu-dispersion , 2004 .