Cohesive modeling of transverse cracking in laminates under in-plane loading with a single layer of elements per ply

Abstract This study aims to bridge the gap between classical understanding of transverse cracking in cross-ply laminates and recent computational methods for the modeling of progressive laminate failure. Specifically, the study investigates under what conditions a finite element model with cohesive X-FEM cracks can reproduce the in situ effect for the ply strength. It is shown that it is possible to do so with a single element across the thickness of the ply, provided that the interface stiffness is properly selected. The optimal value for this interface stiffness is derived with an analytical shear lag model. It is also shown that, when the appropriate statistical variation of properties has been applied, models with a single element through the thickness of a ply can predict the density of transverse matrix cracks.

[1]  L. J. Sluys,et al.  Computational modeling of complex failure mechanisms in laminates , 2012 .

[2]  Pedro P. Camanho,et al.  Failure Criteria for FRP Laminates , 2005 .

[3]  Ted Belytschko,et al.  A finite element method for crack growth without remeshing , 1999 .

[4]  P.P. Camanho,et al.  A Three-dimensional Damage Model for Transversely Isotropic Composite Laminates , 2008 .

[5]  L. J. Sluys,et al.  A phantom node formulation with mixed mode cohesive law for splitting in laminates , 2009 .

[6]  L. J. Sluys,et al.  Mesh-independent modeling of both distributed and discrete matrix cracking in interaction with delamination in composites , 2010 .

[7]  J. Nairn,et al.  The Formation and Propagation of Matrix Microcracks in Cross-Ply Laminates during Static Loading , 1992 .

[8]  D. Borst,et al.  Analysis of fracture and delamination in laminates using 3D numerical modelling , 2009 .

[9]  J. E. Bailey,et al.  Multiple transverse fracture in 90° cross-ply laminates of a glass fibre-reinforced polyester , 1977 .

[10]  A.S.D. Wang,et al.  The Dependence of Transverse Cracking and Delamination on Ply Thickness in Graphite/Epoxy Laminates , 1982 .

[11]  J. Berthelot,et al.  Transverse cracking and delamination in cross-ply glass-fiber and carbon-fiber reinforced plastic laminates: Static and fatigue loading , 2003 .

[12]  Pedro P. Camanho,et al.  A damage model for the simulation of delamination in advanced composites under variable-mode loading , 2006 .

[13]  Norman Laws,et al.  Analysis of Progressive Matrix Cracking In Composite Laminates II. First Ply Failure , 1987 .

[14]  Pedro P. Camanho,et al.  Prediction of in situ strengths and matrix cracking in composites under transverse tension and in-plane shear , 2006 .

[15]  Endel Iarve,et al.  Mesh‐independent matrix cracking and delamination modeling in laminated composites , 2011 .

[16]  Frans P. van der Meer,et al.  Mesolevel Modeling of Failure in Composite Laminates: Constitutive, Kinematic and Algorithmic Aspects , 2012 .

[17]  B. Cox,et al.  The evolution of a transverse intra-ply crack coupled to delamination cracks , 2010 .

[18]  Tsu-Wei Chou,et al.  Statistical analysis of multiple fracture in 0°/90°/0° glass fibre/epoxy resin laminates , 1983 .

[19]  Pedro P. Camanho,et al.  Accurate simulation of delamination growth under mixed-mode loading using cohesive elements: Definition of interlaminar strengths and elastic stiffness , 2010 .

[20]  P. T. Curtis,et al.  On the transverse cracking and longitudinal splitting behaviour of glass and carbon fibre reinforced epoxy cross ply laminates and the effect of Poisson and thermally generated strain , 1979, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[21]  Asd Wang,et al.  Fracture Mechanics of Sublaminate Cracks in Composite Materials , 1984 .

[22]  J. Berthelot,et al.  Statistical analysis of the progression of transverse cracking and delamination in cross-ply laminates , 2000 .

[23]  John A. Nairn,et al.  2.12 – Matrix Microcracking in Composites , 2000 .

[24]  Daosheng Ling,et al.  An augmented finite element method for modeling arbitrary discontinuities in composite materials , 2009 .

[25]  George J. Dvorak,et al.  Progressive Transverse Cracking In Composite Laminates , 1988 .

[26]  Zvi Hashin,et al.  Finite thermoelastic fracture criterion with application to laminate cracking analysis , 1996 .

[27]  Z. Suo,et al.  Mixed mode cracking in layered materials , 1991 .

[28]  J. E. Bailey,et al.  Constrained cracking in glass fibre-reinforced epoxy cross-ply laminates , 1978 .

[29]  J. Segurado,et al.  Intraply fracture of fiber-reinforced composites: Microscopic mechanisms and modeling , 2012 .

[30]  C. Dávila,et al.  Modeling transverse cracking in laminates with a single layer of elements per ply , 2012 .

[31]  F. Chang,et al.  Modelling of splitting and delamination in notched cross-ply laminates , 2000 .