Melt fracture behavior of polypropylene‐type resins with narrow molecular weight distribution. I. Temperature dependence

Polypropylene (PP)-type resins with narrow molecular weight distribution, such as PP-type thermoplastic elastomer PER and controlled-rheology PP (CRPP) made by peroxide degradation of high molecular weight PP, have a problem of easy generation of skin roughness at extrusion. To examine the present state, the occurrence of skin roughness in PER and CRPP at extrusion was investigated with a capillary rheometer in a shear rate range of 12–6100 s−1 and a temperature range of 180–280°C. A homo-PP (HPP) and a block-PP (BPP) with usual molecular weight distributions were used for comparison. HPP and BPP with usual molecular weight distributions show smooth extrudates at low shear rates and abruptly generate severe skin roughness “elastic failure” originating at the die entrance at a higher shear rate. PER and CRPP with narrow molecular weight distributions easily generate “sharkskin” melt fracture originating at the die exit, from a shear rate nearly one decade lower than rates of elastic failure of HPP and BPP. The sharkskin becomes more severe, with increasing shear rate, and attains to the elastic failure. The critical shear rate at which sharkskin occurs increases with increasing extrusion temperature. The critical shear rate is about 20 s−1 at 180°C and about 120 s−1 at 280°C, which is in the range encountered by the molten resin at extrusion processing. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2111–2119, 2002

[1]  M. Denn,et al.  Disappearance of extrusion instabilities in brass capillary dies , 1999 .

[2]  M. Shaw,et al.  Visual observation of development of sharkskin melt fracture in polybutadiene extrusion , 1998 .

[3]  Shi‐Qing Wang,et al.  INTERFACIAL MOLECULAR INSTABILITY MECHANISM FOR SHARKSKIN PHENOMENON IN CAPILLARY EXTRUSION OF LINEAR POLYETHYLENES , 1998 .

[4]  J. Piau,et al.  Sharkskin and cracking of polymer melt extrudates , 1997 .

[5]  Shi‐Qing Wang,et al.  Exploring molecular origins of sharkskin, partial slip, and slope change in flow curves of linear low density polyethylene , 1996 .

[6]  S. Hatzikiriakos,et al.  The effect of teflon™ coatings in polyethylene capillary extrusion , 1995 .

[7]  J. Piau,et al.  Adhesion of linear low density polyethylene for flow regimes with sharkskin , 1994 .

[8]  B. Tremblay Sharkskin defects of polymer melts: The role of cohesion and adhesion , 1991 .

[9]  R. Ramanathan,et al.  Additional observations on the surface melt fracture behavior of linear low-density polyethylene , 1990 .

[10]  J. Piau,et al.  Influence of upstream instabilities and wall slip on melt fracture and sharkskin phenomena during silicones extrusion through orifice dies , 1990 .

[11]  N. E. Kissi,et al.  The different capillary flow regimes of entangled polydimethylsiloxane polymers : macroscopic slip at the wall, hysteresis and cork flow , 1990 .

[12]  Hiroyuki Kobayashi,et al.  High-shear Viscoelastic Properties of Molten Polyethylene and Unstable Flow Mechanisms , 1989 .

[13]  Douglass S. Kalika,et al.  Wall Slip and Extrudate Distortion in Linear Low‐Density Polyethylene , 1987 .

[14]  A. V. Ramamurthy Wall Slip in Viscous Fluids and Influence of Materials of Construction , 1986 .

[15]  F. Cogswell Stretching flow instabilities at the exits of extrusion dies , 1977 .

[16]  J. Tordella Capillary Flow of Molten Polyethylene—A Photographic Study of Melt Fracture , 1957 .

[17]  M. Mooney Explicit Formulas for Slip and Fluidity , 1931 .